Decorative articles with portions in relief and methods of making same
A decorative article of manufacture includes a substrate having a surface of thermoplastic material and one or more relief portions extending from the substrate surface. The one or more relief portions are formed from a blend of powdered thermoplastic material and powdered non-thermoplastic material, wherein the powdered non-thermoplastic material is selected from the group consisting of metals, glass, minerals, and combinations thereof, wherein the powdered thermoplastic material is fused together and to the substrate thermoplastic material.
1. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material;
heating the thermoplastic powder such that the thermoplastic powder fuses together;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
2. The method of claim 1 , wherein the thermoplastic powder is heated to a temperature greater than about 280° F. for about fifteen minutes.
3. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material, wherein applying a compressive force to the substrate and mold comprises:
applying a compressive force of at least about 50 psi to the substrate and mold at a temperature greater than about 280° F. for a first period of time; and
applying a compressive force of at least about 50 psi to the substrate and mold at a temperature less than about 180° F. for a second period of time; and
removing the article of manufacture from the mold.
4. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder and powdered non-thermoplastic material blended therewith;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
5. The method of claim 4 , wherein the powdered non-thermoplastic material is selected from the group consisting of metals, glass, minerals, thermoset plastics, and combinations thereof.
6. The method of claim 1 , wherein the thermoplastic powder comprises material selected from the group consisting of acrylonitrile butadiene styrene, polyethylene, polypropylene, polyolefin, poly vinyl chloride, acrylics, polycarbonates, styrenes, acetyls, polyvinyls, and combinations thereof.
7. The method of claim 1 , wherein the substrate comprises thermoplastic material selected from the group consisting of acrylonitrile butadiene styrene, polyethylene, polypropylene, polyolefin, poly vinyl chloride, acrylics, polycarbonates, styrenes, acetyls, polyvinyls, and combinations thereof.
8. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises a blend of multiple, different powdered thermoplastic materials;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
9. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material, wherein the powder and substrate have different colors;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
10. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses in a transparent state to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
11. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material and indicia;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
12. A method of producing a decorative article of manufacture, comprising:
depositing a layer of powder onto a mold surface, wherein the powder comprises thermoplastic powder;
placing a substrate in contacting relationship with the layer of thermoplastic powder, wherein the substrate comprises thermoplastic material and one or more textured surfaces;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
13. A method of producing a decorative article of manufacture having at least one relief portion extending therefrom, the method comprising:
depositing powder into one or more recesses formed within a mold surface, such that the powder is not in contact with the mold surface, wherein the powder comprises thermoplastic material;
placing a substrate surface in contacting relationship with the mold surface, wherein the substrate comprises thermoplastic material;
applying a compressive force to the substrate and mold such that the thermoplastic powder becomes thermoformable without liquefying, and fuses to the substrate thermoplastic material; and
removing the article of manufacture from the mold.
14. The method of claim 13 , further comprising heating the thermoplastic powder such that the thermoplastic powder fuses together prior to applying a compressive force to the substrate and mold.
15. The method of claim 14 , wherein the thermoplastic powder is heated to a temperature greater than about 280° F. for about fifteen minutes.
16. The method of claim 13 , wherein applying a compressive force to the substrate and mold comprises:
applying a compressive force of at least about 50 psi to the substrate and mold at a temperature greater than about 280° F. for a first period of time; and
applying a compressive force of at least about 50 psi to the substrate and mold at a temperature less than about 180° F. for a second period of time.
17. The method of claim 13 , wherein the thermoplastic powder comprises powdered non-thermoplastic material blended therewith.
18. The method of claim 17 , wherein the powdered non-thermoplastic material is selected from the group consisting of metals, glass, minerals, thermoset plastics, and combinations thereof.
19. The method of claim 13 , wherein the thermoplastic powder comprises material selected from the group consisting of acrylonitrile butadiene styrene, polyethylene, polypropylene, polyolefin, poly vinyl chloride, acrylics, polycarbonates, styrenes, acetyls, polyvinyls, and combinations thereof.
20. The method of claim 13 , wherein the substrate comprises thermoplastic material selected from the group consisting of acrylonitrile butadiene styrene, polyethylene, polypropylene, polyolefin, poly vinyl chloride, acrylics, polycarbonates, styrenes, acetyls, polyvinyls, and combinations thereof.
21. The method of claim 13 , wherein the thermoplastic powder comprises a blend of multiple, different powdered thermoplastic materials.
22. The method of claim 13 , wherein the powder and substrate have different colors.
23. The method of claim 13 , wherein the thermoplastic powder fuses to a transparent state.
24. The method of claim 13 , wherein the substrate comprises indicia.
25. The method of claim 13 , wherein the substrate comprises one or more textured surfaces.
26. The method of claim 13 , wherein the one or more recesses comprises a configuration of a respective alphanumeric character.