Electrode structure for solid polymer fuel cell, its production method, and solid polymer fuel cell
An electrode structure having a pair of electrode catalyst layers and a polymer electrolyte membrane held between both the electrode catalyst layers is provided. The polymer electrolyte membrane is a sulfonate of a hydrocarbon-based polymer comprising a main chain in which two or more benzene rings are bound together directly or through a divalent group. The membrane includes 5% or more by weight of water coordinated to protons of sulfonic acid groups. The polymer electrolyte membrane may include a fluorine-containing ion conducting polymer such that the ratio of fluorine content in the polymer electrolyte membrane to the fluorine content in the electrode catalyst layers is in the range of from 0.2 to 2.0. The electrode structure constitutes a fuel cell, which generates power when oxidizing gas is supplied to the one side of the electrode structure and reducing gas to the other side.
1. An electrode structure for a polymer electrolyte fuel cell comprising a pair of electrode catalyst layers and a polymer electrolyte membrane sandwiched between the electrode catalyst layers,
wherein said polymer electrolyte membrane is a sulfonate of a hydrocarbon-based polymer comprising a main chain, in which a plurality of benzene rings are bound to one another, directly or through a divalent organic group, and
wherein said polymer electrolyte membrane comprises an ion conducting polymer containing fluorine in a molecular structure thereof, and the ratio (Y/X) of the fluorine content in said polymer electrolyte membrane (Y) to the fluorine content in said electrode catalyst layer (X) is within the range of 0.2 to 2.0.
2. The electrode structure for a polymer electrolyte fuel cell according to claim 1 , wherein said polymer electrolyte membrane contains 5% or more by weight of the water coordinated to protons of sulfonic acid groups based on the total weight of the polymer electrolyte membrane.
3. The electrode structure for a polymer electrolyte fuel cell according to claim 1 , wherein that said polymer electrolyte membrane consists of a sulfonate of a copolymer of a first repeating unit represented by the following general formula (1) and a second repeating unit represented by the following general formula (2), and in that the first repeating unit or the second repeating unit contains fluorine:
wherein A represents an electron attracting group, B represents an electron releasing group, n is an integer of 0 or 1, and each benzene ring represents one of benzene and a derivative thereof, and
wherein A represents an electron attracting group, B represents an electron releasing group, Y represents —C(CF 3 ) 2 — or —SO 2 — and each benzene ring represents one of benzene and a derivative thereof.
4. The electrode structure for a polymer electrolyte fuel cell according to claim 1 , wherein that said polymer electrolyte membrane consists of a sulfonate of a copolymer of a first repeating unit represented by the following general formula (1) and a second repeating unit represented by the following general formula (2), and
in that said electrode catalyst layer contains, as a catalyst, platinum within the range of from 0.01 to 0.8 mg/cm 2 , and the average diameter of a carbon particle as a carrier supporting the platinum is within the range of from 10 to 100 nm:
wherein A represents an electron attracting group, B represents an electron releasing group, n is an integer of 0 or 1, and each benzene ring represents one of benzene and a derivative thereof, and
wherein A represents an electron attracting group, B represents an electron releasing group, Y represents —C(CF 3 ) 2 — or —SO 2 —, and each benzene ring represents one of benzene and a derivative thereof.
5. The electrode structure for a polymer electrolyte fuel cell according to claim 4 , wherein said copolymer comprises from 10 to 80 mol % of said first repeating unit and from 90 to 20 mol % of said second repeating unit.
6. The electrode structure for a polymer electrolyte fuel cell according to claim 4 or 5 , wherein the sulfonate of said copolymer contains a sulfonic acid group within the range of from 0.5 to 3.0 mg equivalent/g.
7. The electrode structure for a polymer electrolyte fuel cell according to claim 1 , wherein said polymer electrolyte membrane is produced by forming a membrane from a solution obtained by dissolving into a solvent a sulfonate of a copolymer of a first repeating unit represented by the following general formula (1) and a second repeating unit represented by the following general formula (2) and drying the obtained membrane, and the polymer electrolyte membrane contains from 3 to 15% by weight of said solvent after drying:
wherein A represents an electron attracting group, B represents an electron releasing group, n is an integer of 0 or 1, and each a benzene ring represents one of benzene and a derivative thereof, and
wherein A represents an electron attracting group, B represents an electron releasing group, Y represents —C(CF 3 ) 2 — or —SO 2 —, and a benzene ring represents one of benzene and a derivative thereof.
8. The electrode structure for a polymer electrolyte fuel cell according to claim 7 , wherein said solvent is N-methylpyrrolidone.
9. The electrode structure for a polymer electrolyte fuel cell according to claim 7 or 8 , characterized in that said copolymer comprises from 10 to 80 mol % of said first repeating unit and from 90 to 20 mol % of said second repeating unit.
10. The electrode structure for a polymer electrolyte fuel cell according to claims 7 to 8 , wherein said copolymer contains sulfonic acid groups within the range from 0.5 to 3.0 mg equivalent/g.
11. A polymer electrolyte fuel cell comprising an electrode structure comprising a pair of electrode catalyst layers and a polymer electrolyte membrane held between the electrode catalyst layers, wherein said polymer electrolyte membrane is a sulfonate of a hydrocarbon-based polymer comprising a main chain, in which two or more benzene rings are bound to one another, directly or through a divalent organic group, said electrode catalyst layers comprise a carbon particle supporting a catalyst particle that is integrated by an ion conducting polymer binder containing fluorine in a molecular structure thereof, said polymer electrolyte membrane comprises an ion conducting polymer containing fluorine in a molecular structure thereof, the ratio (Y/X) of the fluorine content in said polymer electrolyte membrane (Y) to the fluorine content in said electrode catalyst layer (X) is within the range of from 0.2 to 2.0, and said polymer electrolyte fuel cell generates power when oxidizing gas is supplied to the one side of said electrode structure and reducing gas to the other side.
12. The polymer electrolyte fuel cell according to claim 11 , wherein said polymer electrolyte membrane is a sulfonate of a copolymer of a first repeating unit represented by the following general formula (1) and a second repeating unit represented by the following general formula (2), said electrode catalyst layer contains, as a catalyst, platinum within the range or from 0.01 to 0.8 mg/cm 2 , and the average diameter of a carbon particle as a carrier supporting the platinum is within the range or from 10 to 100 nm:
wherein A represents an electron attracting group, B represents an electron releasing group, n is an integer of 0 or 1, and each benzene ring represents one of benzene and a derivative thereof, and
wherein A represents an electron attracting group, B represents an electron releasing group, Y represents —C(CF 3 ) 2 — or —SO 2 —, and each benzene ring represents one of benzene and a derivative thereof.
13. The polymer electrolyte fuel cell according to claim 11 , wherein said polymer electrolyte membrane is produced by forming a membrane from a solution obtained by dissolving into a solvent a sulfonate of a copolymer of a first repeating unit represented by the following general formula (1) and a second repeating unit represented by the following general formula (2) and drying the obtained membrane, and in that the membrane contains from 3 to 15% by weight of said solvent after drying:
wherein A represents an electron attracting group, B represents an electron releasing group, n is an integer of 0 or 1, and each benzene ring represents one of benzene and a derivative thereof, and
wherein A represents an electron attracting group, B represents an electron releasing group, Y represents —C(CF 3 ) 2 — or —SO 2 —, and each benzene ring represents one of benzene and a derivative thereof.
14. The polymer electrolyte fuel cell according to claim 11 , wherein said electrode structure is formed by holding a polymer electrolyte membrane between a pair of electrode catalyst layers to integrate both the electrode catalyst layers and the polymer electrode membrane, and applying an electric current of 0.1 A/cm 2 or higher to integrated body of the electrode catalyst layers and the polymer electrolyte membrane for 5 hours or more in a humidified environment at a relative humidity of 60% or more.