Stable anodes including iron oxide and use of such anodes in metal production cells
Stable anodes comprising iron oxide useful for the electrolytic production of metal such as aluminum are disclosed. The iron oxide may comprise Fe 3 O 4 , Fe 2 O 3 , FeO or a combination thereof. During the electrolytic aluminum production process, the anodes remain stable at a controlled bath temperature of the aluminum production cell and current density through the anodes is controlled. The iron oxide-containing anodes may be used to produce commercial purity aluminum.
1. A method of producing aluminum comprising:
passing current between a stable anode comprising iron oxide and a cathode through a bath comprising an electrolyte and aluminum oxide;
maintaining the bath at a controlled temperature;
controlling current density through the anode; and
recovering aluminum from the bath,
wherein the stable anode is a monolithic body entirely composed of Fe 3 O 4 , Fe 3 O 2 and, FeO and optional additives or dopants, wherein at least about 80 wt. % of the stable anode comprises Fe 2 O 3 , Fe 3 O 4 or a combination thereof, and wherein the stable anode comprises up to about 20 wt. % FeO, wherein at least some FeO is present in the stable anode.
2. The method of claim 1 , wherein the controlled temperature of the bath is less than about 960° C.
3. The method of claim 1 , wherein the controlled temperature of the bath is from about 800 to about 930° C.
4. The method of claim 1 , wherein the current density is from about 0.1 to about 6 Amp/cm 2 .
5. The method of claim 1 , wherein the current density is from about 0.25 to about 2.5 Amp/cm 2 .
6. The method of claim 1 , wherein the stable anode comprises at least about 90 wt. % of Fe 2 O 3 , Fe 3 O 4 or a combination thereof, and up to about 10 wt. % FeO, wherein at least some FeO is present in the stable anode.
7. The method of claim 1 , wherein the stable anode includes at least some of the optional additive or dopant.
8. The method of claim 7 , wherein the additive comprises an oxide of Al, Si, Ca, Mn and/or Mg.
9. The method of claim 1 , wherein the recovered aluminum comprises less than about 0.5 weight percent Fe.
10. The method of claim 1 , wherein the recovered aluminum comprises less than about 0.4 weight percent Fe.
11. The method of claim 1 , wherein the recovered aluminum comprises less than about 0.3 weight percent Fe.
12. The method of claim 1 , wherein the recovered aluminum comprises a maximum of about 0.2 weight percent Fe, a maximum of about 0.034 weight percent Cu, and a maximum of about 0.034 weight percent Ni.
13. The method of claim 1 , wherein the recovered aluminum is commercial purity aluminum.