Positive electrode active material for non-aqueous electrolyte secondary battery and manufacturing method thereof, and non-aqueous electrolyte secondary battery using same

1. A positive electrode active material for a non-aqueous electrolyte secondary battery comprising:

primary particles of a lithium-metal complex oxide powder which is a lithium-metal complex oxide powder represented by Li z Ni 1-w M w O 2 , wherein M is at least one metal element selected from the group consisting of Co, Al, Mg, Mn, Ti, Fe, Cu, Zn, and Ga; and w and z respectively satisfy 0<w≦0.25, and 1.0≦z≦1.1; and

secondary particles which are formed by aggregating a plurality of the primary particles,

wherein:

the shape of the secondary particles is spherical or spheroidal;

95% or more of the secondary particles have particle diameters of 20 μm or less;

a mean particle diameter of the secondary particles is between 7 and 13 μm;

a tap density of the particles is 2.2 g/cm 3 or more;

in a pore distribution measurement using a nitrogen adsorption method, a mean volume of pores having a diameter of 40 nm or less in average is between 0.001 and 0.008 cm 3 /g; and

a mean crushing strength of the secondary particles is between 15 and 100 MPa.

2. A positive electrode active material for a non-aqueous electrolyte secondary battery comprising:

primary particles of a lithium-metal complex oxide powder which is a lithium-metal complex oxide powder represented by Li z Ni 1−x−y T x L y O 2 , wherein T is at least one metal element selected from the group consisting of Co, and Mn; L is at least one metal element selected from the group consisting of Al, Mg, Ti, Fe, Cu, Zn, and Ga; and x, y, and z respectively satisfy 0<x<0.25, 0<y≦0.1, 0<x+y≦0.25, and 1.0≦z≦1.1; and

secondary particles which are formed by aggregating a plurality of the primary particles, wherein:

the shape of the secondary particles is spherical or spheroidal;

95% or more of the secondary particles have particle diameters of 20 μm or less;

a mean particle diameter of the secondary particles is between 7 and 13 μm;

a tap density of the particles is 2.2 g/cm 3 or more;

in a pore distribution measurement using a nitrogen adsorption method, a mean volume of pores having a diameter of 40 nm or less in average is between 0.001 and 0.008 cm 3 /g; and

a mean crushing strength of the secondary particles is between 15 and 100 MPa.

3. A positive electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 or claim 2 , wherein for the lithium-metal complex oxide, on 3a sites where Li ions are to be arranged in a layered rock-salt structure of LiNiO 2 , a site occupancy rate of metal ions other than Li ion is 2% or less.

4. A positive electrode active material for a non-aqueous electrolyte secondary battery according to claim 1 or claim 2 , wherein the primary particles in the secondary particles are generally arranged radially from a center of the secondary particles.

5. A non-aqueous electrolyte secondary battery comprising a positive electrode wherein said positive comprises a positive electrode active material according to claim 1 or claim 2 .

6. A manufacturing method for a positive electrode active material for a non-aqueous electrolyte secondary battery comprising:

a first step for producing a metal complex hydroxide containing Ni and metal M wherein:

M is at least one metal element selected from the group consisting of Co, Al, Mg, Mn, Ti, Fe, Cu, Zn, and Ga;

said metal complex hydroxide has a proportion of Ni:M=1−w:w (0<w≦0.25) in an atomic number ratio; and a tap density of 1.7 g/cm 3 or more;

a second step for weighing the metal complex hydroxide obtained in the first step and lithium hydroxide so that a ratio of an atomic number of Li to a total atomic number of Ni and metal M is between 1.0 and 1.1, and mixing to obtain a compound; and

a third step for raising the temperature of the compound obtained in the second step, from room temperature to 450 to 550° C. at a temperature rise rate of 0.5 to 15° C./min, holding for 1 to 10 hours at the reaching temperature, and performing first stage baking, and then further raising the temperature to 650 to 800° C. at a temperature rise rate of 1 to 5° C./min, holding for 0.6 to 30 hours at the reaching temperature, and performing second stage baking, and then furnace cooling to obtain a positive electrode active material for a non-aqueous electrolyte secondary battery.

7. A manufacturing method for a positive electrode active material for a non-aqueous electrolyte secondary battery comprising:

a first step for producing a metal complex hydroxide containing Ni and metal T wherein:

T is at least one metal element selected from the group consisting of Co and Mn; and

said metal complex hydroxide has a proportion of Ni:T=1−x−y:x (0<x<0.25, 0<y≦0.1, and 0<x+y≦0.25) in an atomic number ratio and a tap density of 1.7 g/cm 3 or more;

a second step for adding a compound of a metal L to the metal complex hydroxide obtained in the first step, L being at least one metal element selected from the group consisting of Al, Mg, Ti, Fe, Cu, Zn, and Ga, and mixing, and producing a compound A containing Ni and metal L with a proportion of Ni:L=1−x−y:y(0<x<0.25, 0<y≦0.1, and 0<x+y≦0.25) in an atomic number ratio;

a third step for weighing the compound A obtained in the second step and lithium hydroxide so that a ratio of an atomic number of Li to a total atomic number of Ni, metal T, and metal L is between 1.0 and 1.1, and mixing to obtain a compound B; and

a fourth step for raising the temperature of the compound B obtained in the third step, from room temperature to 450 to 550° C. at a temperature rise rate of 0.5 to 15° C./min, holding for 1 to 10 hours at the reaching temperature, and performing first stage baking, and then further raising the temperature to 650 to 800° C. at a temperature rise rate of 1 to 5° C./min, holding for 0.6 to 30 hours at the reaching temperature, and performing second stage baking, and then furnace cooling to obtain a positive electrode active material for a non-aqueous electrolyte secondary battery.

8. A manufacturing method for a positive electrode active material for a non-aqueous electrolyte secondary battery comprising:

a first step for producing a metal complex hydroxide containing Ni, metal T, and metal L wherein:

T is at least one kind or more of metal elements selected from the Group consisting of Co and Mn;

L is at least one kind or more of metal elements selected from the group consisting of Al, Mg, Ti, Fe, Cu, Zn, and Ga; and

said metal complex hydroxide has a proportion of Ni:T:L=1−x−y:x:y (0<x<0.25, 0<y≦0.1, and 0<x+y≦2.5) in an atomic number ratio, and a tap density of 1.7 g/cm 3 or more;

a second step for weighing the metal complex hydroxide obtained in the first step and lithium hydroxide so that a ratio of an atomic number of Li a total atomic number of Ni, metal T, and metal L is between 1.0 and 1.1, and mixing to obtain a compound; and

a third step for raising the temperature of the compound obtained in the second step, from room temperature to 450 to 550° C. at a temperature rise rate of 0.5 to 15° C./min, holding for 1 to 10 hours at the reaching temperature, and performing first stage baking, and then further raising the temperature to 650 to 800° C. at a temperature rise rate of 1 to 5° C./min, holding for 0.6 to 30 hours at the reaching temperature, and performing second stage baking, and then furnace cooling to obtain a positive electrode active material for a non-aqueous electrolyte secondary battery.