Method for making wick structure of heat pipe and powders for making the same
A group of powders ( 40 ) for making a wick structure of a heat pipe includes main powders ( 50 ) and supplemental powders ( 60 ). The melting point of the supplemental powder is lower than that of the main powder. During a sintering process, the powders are filled in a casing of the heat pipe and have a eutectic reaction between the main powders and the supplemental powders to form the wick structure. The temperature for the eutectic reaction is lower than the melting temperature of the supplemental powders.
1. A method of manufacturing a wick structure for a heat pipe comprising steps of:
providing a group of powders comprising a kind of main powders and a kind of supplemental powders having a melting point lower than that of the main powders, the main powders and the supplemental powders being thoroughly mixed;
filling the group of powders into a casing of the heat pipe; and
sintering the powders at a temperature no higher than the melting temperature of the supplemental powders;
wherein the supplemental powders are nano-particles; and
wherein the nano-particles are made of one of the following materials: copper, gold,
aluminum, zinc, tin, nickel, and silver and the main powders are made of a material the same as that for making the supplemental powders.
2. The method of claim 1 , wherein a volume of the supplemental powders is
not larger than 30% than a volume of the group of powders.
3. The method of claim 1 , wherein a powder size of the main powders is larger than that of the supplemental powders.
4. The method of claim 1 , wherein the main powders are made of copper, an expansion ratio of the copper powders during the sintering process is not larger than 2%.
5. The method of claim 1 , wherein the sintering temperature is the melting temperature of the supplemental powders.
6. A group of powders for making a wick structure of a heat pipe comprising:
a kind of main powders; and
a kind of supplemental powders thoroughly mixed with the main powders, the supplemental powders having a melting point lower than that of the main powders, the group of powders being sintered at a temperature no higher than the melting temperature of the supplemental powders to make the wick structure;
wherein the main powders and the supplemental powders are made of same metal, and the supplemental powders are nano-particles having a powder size of 1˜100 nm.
7. The powders of claim 6 , wherein the supplemental powders are made of one of following metals: aluminum, zinc, silver, tin, copper, gold, nickel, and the main powders have a powder size larger than that of the supplemental powders.
8. The powders of claim 6 , wherein the sintering temperature is the melting temperature of the supplemental powders.