Anti-reflective coating
An anti-reflection coating comprising a first polymeric layer having a refractive index between about 1.64 and about 1.85 is disposed on a substrate. A second polymeric layer is also provided having a refractive index between about 1.29 and about 1.55, and overlies the first polymeric layer. An inorganic metal oxide layer 30 also overlies the first polymeric layer.
1. An anti-reflection coating comprising:
a first polymeric layer having a refractive index between about 1.64 and about 1.85, the first polymeric layer being disposed on a substrate, the first polymeric layer comprising a polyelectrolyte, the polyelectrolyte including a plurality of aromatic groups and nitrogen atoms in a main polymer chain, all the aromatic groups in the main polymer chain being arranged in a substantially coplanar manner, the polyelectrolyte having a refractive index of at least about 1.64 at a wavelength of about 680 nm;
a second polymeric layer having a refractive index between about 1.29 and about 1.55 overlying the first polymeric layer; and
an inorganic layer overlying the first polymeric layer.
2. The coating of claim 1 , the inorganic layer having a thickness between about 5 nm to about 200 nm.
3. The coating of claim 1 , the first polymeric layer comprising a plurality of uniformly dispersed colloidal particles.
4. The coating of claim 1 , the polyelectrolyte being formed from a dianhydride.
5. The coating of claim 1 , the second polymeric layer comprising an actinic radiation curable composition, the actinic radiation curable composition having a refractive index between about 1.35 and about 1.55.
6. The coating of claim 1 , the second polymeric layer comprising at least one of a fluorinated material or an air-dry aliphatic resin.
7. The coating of claim 1 , the inorganic layer comprising a sputtered inorganic material.
8. The coating of claim 1 , the second polymeric layer being coated with a reactive fluoro-silicone layer.
9. The coating of claim 1 , the oxide layer having a refractive index that is higher than the refractive index of the first polymeric layer.
10. The coating of claim 1 , the inorganic layer comprising at least one oxide selected from the group consisting of titanium dioxide, indium tin oxide, zirconium oxide, bismuth oxide, hafnium oxide, antimony oxide, tin oxide, tantalum oxide, indium oxide, niobium pentoxide, zinc oxide, and mixtures thereof.
11. The coating of claim 1 , the inorganic layer being interposed between the first polymeric layer and the second polymeric layer.
12. The coating of claim 1 , the second polymer layer being interposed between the inorganic layer and the first polymeric layer.
13. An anti-reflection coating comprising:
a first polymeric layer having a refractive index between about 1.64 and about 1.85, and further having a thickness between about 20 nm and about 250 nm, the first polymeric layer being disposed onto a substrate, the first polymeric layer comprising a polyelectrolyte formed from a dianhydride, the dianhydride including a plurality of aromatic groups arranged in a substantially coplanar manner and all the aromatic groups in a main polymer chain of the polyelectrolyte arranged in a substantially coplanar manner and all the aromatic groups in a main polymer chain of the polyelectrolyte arranged in a substantially coplanar manner;
a second polymeric layer having a refractive index between about 1.29 and about 1.55; and
an inorganic layer having a thickness between about 5 nm and about 200 nm, and further having a refractive index higher than the first polymeric layer, the inorganic layer being interposed between the first polymeric layer and the second polymeric layer.
14. The coating of claim 13 , the polyelectrolyte including a plurality of aromatic groups and nitrogen atoms in a main polymer chain, the polyelectrolyte having a refractive index of at least about 1.64 at a wavelength of about 680 nm.
15. The coating of claim 13 , the inorganic layer comprising a sputtered inorganic material.
16. The coating of claim 15 , the inorganic layer comprising at least one oxide selected from the group consisting of titanium dioxide, indium tin oxide, zirconium oxide, bismuth oxide, hafnium oxide, antimony oxide, tin oxide, tantalum oxide, indium oxide, niobium pentoxide, zinc oxide, and mixtures thereof.
17. An anti-reflection coating comprising:
a first polymeric layer having a refractive index between about 1.64 and about 1.85 at a wavelength of about 680 nm, and further having a thickness between about 20 nm and about 250 nm, the first polymeric layer comprising a polyelectrolyte formed from a dianhydride, the dianhydride including a plurality of aromatic groups arranged in a substantially coplanar manner, all the aromatic groups in a main polymer chain of the polyelectrolyte arranged in a substantially coplanar manner, the first polymeric layer being disposed onto a substrate;
an inorganic layer having a thickness between about 5 nm and about 200 nm, and further having a refractive index higher than the first polymeric layer; and
a second polymeric layer having a refractive index between about 1.29 and about 1.55, the second polymeric layer being interposed between the first polymeric layer and the inorganic layer.
18. The coating of claim 17 , the polyelectrolyte including a plurality of aromatic groups and nitrogen atoms in a main polymer chain, the polyelectrolyte having a refractive index of at least about 1.64 at a wavelength of about 680 nm.
19. The coating of claim 17 , the inorganic layer comprising at least one sputtered metal oxide selected from the group consisting of titanium dioxide, indium tin oxide, zirconium oxide, bismuth oxide, hafnium oxide, antimony oxide, tin oxide, tantalum oxide, indium oxide, niobium pentoxide, zinc oxide, and mixtures thereof.