Formulated resin component for use in spray-in-place foam system to produce a low density polyurethane foam
The subject invention provides an open-celled polyurethane foam formed from a polyurethane spray foam system that mixes a formulated resin component with an isocyanate component. The resultant open-celled polyurethane spray foam has a density of about ½ pound per cubic foot. The resin component includes water as a blowing agent, a first aliphatic, amine-initiated polyol having a number-average molecular weight of from 150 to 500 and having tetra-functionality, and a second polyol having terminal hydroxyl groups and having a number-average molecular weight of from 3500 to 8000. A curing component having at least one primary amine group and having a number-average molecular weight of from 150 to 5000 is also included in the resin component. The spray foam system reacts a) the resin component and b) the isocyanate component in a volumetric ratio of a) to b) of from 1:1.2 to 1:5 and having an isocyanate index of from 15 to 70.
1. A polyurethane foam for insulating structures that is produced from a polyurethane spraying system, said polyurethane foam being the reaction product of:
a) a resin component comprising;
a blowing agent present in an amount of from 15 to 40 parts by weight based on 100 parts by weight of said resin component,
a first polyol used in an amount of from 5 to 25 parts by weight based on 100 parts by weight of said resin component and having a number-average molecular weight of from 150 to 500 and having a hydroxyl number of from 250 to 1000 and having at least tetra-functionality,
a second polyol having a number-average molecular weight of from 3500 to 8000 and having a hydroxyl number of from 20 to 100 and having terminal hydroxyl groups, and
a curing component used in an amount of from 2 to 15 parts by weight based on 100 parts by weight of said resin component and comprising a polyether amine having at least one primary amine group, an equivalent hydroxyl number of from 20 to 800, and having a number-average molecular weight of from 150 to 5000, and
b) an isocyanate component comprising diphenylmethane diisocyanate;
wherein said a) and b) are reacted in a volumetric ratio having an isocyanate index of from 25 to 60; and
wherein said polyurethane foam is open-celled and has a density of less than 1 pound per cubic foot and low water absorption as a result of reacting said a) and b) in said volumetric ratio at said isocyanate index.
2. A polyurethane foam as set forth in claim 1 wherein said polyurethane foam has a water absorption of less than 10 percent by volume of said polyurethane foam.
3. A polyurethane foam as set forth in claim 1 wherein said polyurethane foam has a water absorption of less than 5 percent by volume of said polyurethane foam.
4. A polyurethane foam as set forth in claim 1 wherein said curing component has a number average molecular weight of from 250 to 2500.
5. A polyurethane foam as set forth in claim 1 wherein said first polyol is further defined as an aliphatic, amine-initiated polyol.
6. A polyurethane foam as set forth in claim 1 wherein said second polyol is used in an amount of from 5 to 25 parts by weight based on 100 parts by weight of said resin component.
7. A polyurethane foam as set forth in claim 1 wherein said second polyol is further defined as a triol.
8. A polyurethane foam as set forth in claim 1 wherein said second polyol is further defined as a diol.
9. A method of forming a polyurethane foam for insulating structures dispensed from a polyurethane spraying system, said method comprising the steps of:
providing a) a resin component including a blowing agent present in an amount of from 15 to 40 parts by weight based on 100 parts by weight of said resin component, a first polyol present in an amount of from 5 to 25 parts by weight based on 100 parts by weight of said resin component and having a number-average molecular weight of from 150 to 500, having a hydroxyl number of from 250 to 1000, and having at least tetra-functionality, a second polyol having a number-average molecular weight of from 3500 to 8000, having a hydroxyl number of from 20 to 100, and having terminal hydroxyl groups, and a curing component present in an amount of from 2 to 15 parts by weight based on 100 parts by weight of said resin component and comprising a polyether amine having at least one primary amine group, an equivalent hydroxyl number of from 20 to 800, and having a number-average molecular weight of from 150 to 5000,
providing b) an isocyanate component comprising diphenylmethane diisocyanate; and
reacting a) and b) in a volumetric ratio of from 1:1.2 to 1:3 such that a) and b) are reacted having an isocyanate index of from 25 to 60 such that the polyurethane foam is open-celled and has a density of less than 1 pound per cubic foot and low water absorption as a result of reacting a) and b) in the volumetric ratio at the isocyanate index.
10. A method as set forth in claim 9 wherein the step of reacting a) and b) is further defined as spraying a) and b).
11. A method as set forth in claim 10 wherein the step of spraying a) and b) is further defined as mixing a) and b) through a nozzle of a spray gun.
12. A method as set forth in claim 9 wherein the curing component has a number average molecular weight of from 250 to 2500.