Bimetallic bond layer for thermal barrier coating on superalloy
A bimetallic bond layer ( 26, 28 ) for a thermal barrier coating or TBC ( 30 ) on a superalloy substrate ( 22 ) for a high temperature environment. An interlayer ( 26 ) is applied on the substrate. A bond coat ( 28 ) comprising a CoNiCrAlY or NiCoCrAlY alloy is applied on the interlayer. A ceramic TBC ( 30 ) such as 8YSZ is applied on the bond coat. The interlayer ( 26 ) is an alloy that is compatible with the substrate and the bond coat, and that blocks or delays diffusion of aluminum from the bond coat into the substrate at high operating temperatures. This preserves aluminum in the bond coat that maintains a beneficial alumina scale ( 29 ) between the bond coat and the TBC. This delays spalling of the TBC, and lengthens the coating and component life.
1. A bimetallic bond layer for a thermal barrier coating on a superalloy component, comprising:
a superalloy substrate;
an interlayer on the substrate;
a bond coat comprising a CoNiCrAlY or NiCoCrAlY alloy on the interlayer;
the interlayer comprising an alloy that blocks or delays diffusion of aluminum from the bond coat into the substrate at an operating temperature over 900° C. via the formation of one or more intermetallic precipitate phases in the interlayer; and
a ceramic thermal barrier coating on the bond coat;
wherein the interlayer comprises a nickel base, at most about 1.75 wt % titanium, at least about 8 wt % chromium, at least about 0.2 wt % aluminum, and at least one element selected from Nd 0.1 to 3 wt %, Re 0.2 to 1.5 wt %, and Hf 0.1-2.0 wt %;
wherein the interlayer comprises a Haynes 230 alloy with addition of said at least one element; and
wherein the substrate comprises an IN-939 alloy, and the ceramic thermal barrier coating comprises porous yttrium stabilized zirconia.
2. The bimetallic bond layer of claim 1 , wherein the interlayer comprises Nd 0.1 to 3 wt %.
3. A bimetallic bond layer for a thermal barrier coating on a superalloy component, comprising:
a superalloy substrate;
an interlayer on the substrate;
a bond coat comprising a CoNiCrAlY or NiCoCrAlY alloy on the interlayer;
the interlayer comprising an alloy that blocks or delays diffusion of aluminum from the bond coat into the substrate at an operating temperature over 900° C. via the formation of one or more intermetallic precipitate phases in the interlayer; and
a ceramic thermal barrier coating on the bond coat;
wherein the interlayer comprises a nickel base, at most about 1.75 wt % titanium, at least about 8 wt % chromium, at least about 0.2 wt % aluminum, and at least one element selected from Nd 0.1 to 3 wt %, Re 0.2 to 1.5 wt %, and Hf 0.1-2.0 wt %; and
wherein the interlayer comprises a Haynes 230 alloy with addition of said at least one element.