Coating precursor materials, turbomachinery components, and methods of forming the turbomachinery components
Coating precursor materials, turbomachinery components, and methods of manufacturing the components are provided. In an embodiment, by way of example only, a coating precursor material includes a solid film lubricant component and a bonding component comprising at least one eutectic mixture, said at least one eutectic mixture selected from a group consisting of barium fluoride/nickel fluoride, barium fluoride/cobalt fluoride, and barium fluoride/barium fluoride-boron oxide.
1. A coating precursor material, comprising:
a solid film lubricant component; and
a bonding component comprising at least one eutectic mixture, the at least one eutectic mixture selected from a group consisting of barium fluoride/nickel fluoride, barium fluoride/cobalt fluoride, and barium fluoride/barium fluoride-boron oxide.
2. The coating precursor material of claim 1 , wherein the solid film lubricant component comprises a material having the chemical formula M n+1 AX n , wherein M is at least one early transition metal selected from groups IIIB, IVB, VB, and VIB, A is at least one element selected from groups IIIA, IVA, VA, VIA, and VIIA, X is one or both of carbon and nitrogen, and n is an integer between 1 and 3.
3. The coating precursor material of claim 1 , wherein the solid film lubricant component comprises one or more metal sulfides, metal fluorides, and/or precious metals.
4. The coating precursor material of claim 3 , wherein a metal sulfide includes MoS 2 .
5. The coating precursor material of claim 3 , wherein a metal fluoride comprises at least one metal selected from a group consisting of a Group IA alkali earth metal, a Group IIA alkaline earth metal, a rare earth metal, and mixtures thereof.
6. The coating precursor material of claim 3 , wherein a precious metal comprises a material selected from a group consisting of silver, gold, platinum, palladium, rhenium, copper, and mixtures thereof.
7. The coating precursor material of claim 1 , further comprising at least one wear-resistant component comprising a metal oxide.
8. The coating precursor material of claim 7 , wherein the metal oxide includes a material selected from a group consisting of chromic oxide, nickel oxide, aluminum oxide, boron oxide or another metal oxide.
9. The coating precursor material of claim 1 , further comprising a non-metallic component including at least one of a ceramic, a silicate, and a binder.
10. The coating precursor material of claim 9 , wherein the ceramic comprises a material selected from a group consisting of Cr 2 O 3 , Al 2 O 3 , and TiO 2 .
11. The coating precursor material of claim 9 , wherein the silicate comprises sodium silicate.
12. The coating precursor material of claim 9 , wherein the binder comprises an organic polymer binder.
13. A turbomachinery component comprising:
a substrate; and
a coating over the substrate, the coating comprising a solid film lubricant component and a bonding component, the bonding component comprising at least one eutectic mixture selected from a group consisting of barium fluoride/nickel fluoride, barium fluoride/cobalt fluoride, and barium fluoride/barium fluoride-boron oxide.
14. The turbomachinery component of claim 13 , wherein the solid film lubricant component comprises a material having the chemical formula M n+1 AX n , wherein M is at least one early transition metal selected from groups IIIB, IVB, VB, and VIB, A is at least one element selected from groups IIIA, IVA, VA, VIA, and VIIA, X is one or both of carbon and nitrogen, and n is an integer between 1 and 3.
15. The turbomachinery component of claim 13 , wherein the solid film lubricant component comprises one or more metal sulfides, metal fluorides, and/or precious metals.
16. The turbomachinery component of claim 13 , further comprising at least one wear-resistant component comprising a metal oxide.
17. The turbomachinery component of claim 13 , wherein the turbomachinery component comprises a foil bearing.
18. A method of manufacturing a turbomachinery component, the method comprising the steps of:
applying a coating precursor material to a substrate, wherein the coating precursor material comprises a solid film lubricant component and a bonding component, and the bonding component comprises at least one eutectic mixture, the at least one eutectic mixture selected from a group consisting of barium fluoride/nickel fluoride, barium fluoride/cobalt fluoride, and barium fluoride/barium fluoride-boron oxide; and
heating the substrate to a predetermined processing temperature to form a portion of a coating over the substrate.
19. The method of claim 18 , wherein the solid film lubricant component comprises a material having the chemical formula M n+1 AX n , wherein M is at least one early transition metal selected from groups IIIB, IVB, VB, and VIB, A is at least one element selected from groups IIIA, IVA, VA, VIA, and VIIA, X is one or both of carbon and nitrogen, and n is an integer between 1 and 3.
20. The method of claim 18 , wherein the solid film lubricant component comprises one or more metal sulfides, metal fluorides, and/or precious metals.