Method for manufacturing liquid crystalline resin composition of reduced density
The object is to provide a method for manufacturing liquid crystalline resin composition having a hollow filler and a fibrous filler using a common melting-kneading extruder to maintain well-balanced relation between the residual percentages of hollow filler and the fiber length, which balance could not be attained in the prior art. A liquid crystalline resin composition having 5 to 30% by weight of hollow filler and 5 to 30% by weight of fibrous filler is manufactured using a melting-kneading extruder provided with a screw. (1) The liquid crystalline resin is fed from a main feed port located at upstream side in the extruding direction, while a hollow filler and a fibrous filler are fed from a side feed port located at downstream side in the extruding direction. The manufacture is conducted under the specific conditions between (2) L 1 as the ratio L/D in which D is the screw diameter and L is the distance between the position of the side feed port and the position where the internal pressure of the extruder reaches 0.1 MPa; (3) L 2 as the ratio L/D in which D is the screw diameter and L is the length of maintaining the internal pressure of the extruder at or above 0.1 MPa after feeding the hollow filler and the fibrous filler; and (4) La as the ratio L/D in which D is the screw diameter and L is the length of the resin plasticizing zone.
1. A method for manufacturing a liquid crystalline resin composition containing both a hollow filler and a fibrous filler that is suitable for injection molding to form an article of reduced density, said composition comprising a liquid crystalline resin, 5 to 30% by weight of hollow filler and 10 to 20% by weight of glass fibrous filler having a weight average fiber length of about 200 μm to about 700 μm, said method using a melting-kneading extruder provided with a screw, comprising a step of:
(1) feeding said liquid crystalline resin from a main feed port located at upstream side in the extruding direction, while feeding said hollow filler and said glass fibrous filler from a side feed port located at downstream side in the extruding direction;
and satisfying the conditions of:
L1>3.5,
4<L2<9,
2<La<6,
Lb>5, and
4<Lc<9,
where:
(2) L 1 designates the ratio L/D in which D is the screw diameter and L is the distance between the position of the side feed port and the position where the internal pressure of the extruder reaches 0.1 MPa;
(3) L 2 designates the ratio L/D in which D is the screw diameter and L is the length of maintaining the internal pressure of the extruder at or above 0.1 MPa after feeding said hollow filler and said glass fibrous filler; and
(4) La designates the ratio L/D in which D is the screw diameter and L is the length of the resin plasticizing zone,
(5) Lb designates the ratio L/D in which D is the screw diameter and L is the distance between the position of the side feed port and the downstream position where kneading begins, and
(6) Lc designates the ratio L/D in which L is the length of the kneading zone and D is the screw diameter, and wherein at least 67% of said hollow filler that is fed from said side port and is present within the resulting liquid crystalline resin composition remains unbroken at the conclusion of said method and is present therein together with said glass fibrous filler that also was fed from said side port.
2. The method for manufacturing liquid crystalline resin composition as in claim 1 , being conducted by a screw satisfying the conditions of:
3<La<6,
6<Lb<10, and
5<Lc<8.
3. The method according to claim 1 , wherein said glass fibrous filler that is fed to said side feed port possesses an average fiber length of about 300 μm to about 600 μm.
4. The method according to claim 1 , wherein L 1 is larger than 5.
5. The method according to claim 1 , wherein L 1 is larger than 10.
6. The method according to claim 1 , wherein said liquid crystalline resin is fully melted before being kneaded with said hollow filler and said glass fibrous filler.
7. The method according to claim 1 , wherein said hollow filler is present in said composition in the range of 10 to 20% by weight.
8. The method according to claim 1 , wherein the average particle size of said hollow filler is 5 μm or larger.
9. The method according to claim 1 , wherein the average particle size of said hollow filler is 10 μm or larger.