Process for fabricating polypropylene sheet
A process of production of a monolithic article from a web of fibres of oriented polypropylene polymer, comprising the steps of subjecting the web to elevated temperature and pressure sufficient to melt a proportion of the polymer and compact it, and then cooling the compacted web, wherein an accelerated rate of cooling is employed down to 100° C. The process is of particular benefit when the weight average molecular weight (M w ) of the fibers is 250,000 or below. The resultant articles have good stiffness and strength, yet with reasonable ductility. Similar articles cooled slowly are brittle.
1. A process for production of a monolithic article from an assembly of two or more webs of fibres of oriented polypropylene homopolymer or copolymer having a melting temperature and a recrystallisation temperature and having a weight average molecular weight of less than or equal to 250,000, comprising the steps of:
subjecting the assembly to elevated temperature and pressure sufficient to melt a proportion of the polymer and compact it; and
actively cooling the compacted assembly at an elevated pressure to a predetermined amount below the recrystallisation temperature, wherein an accelerated rate of cooling is employed down to the predetermined amount below the recrystallisation temperature of the fibres at an accelerated cooling rate of at least 35° C. per minute, such as to produce a monolithic article with improved ductility and improved peel strength.
2. A process for the production of a monolithic article from an assembly of two or more webs of fibres of oriented polypropylene homopolymer or copolymer having a weight average molecular weight of less than or equal to 250,000, comprising the steps of subjecting the assembly to elevated temperature and pressure sufficient to melt a proportion of the polymer and compact it, and then actively cooling the compacted assembly at an elevated pressure, wherein an accelerated rate of cooling of at least 35° C. per minute is employed down to 100° C., such as to produce a monolithic article with improved ductility and improved peel strength.
3. A process as claimed in claim 1 wherein the compaction pressure does not exceed 10 MPa.
4. A process as claimed in claim 1 , wherein the fibres are melt formed fibres.
5. A process as claimed in claim 1 wherein the weight average molecular weight (M w ) of the fibres is in the range 100,000 to 250,000.
6. A process as claimed in claim 1 wherein the weight average molecular weight (M w ) of the fibres is in the range 150,000 to 220,000.