Method and structure for nonlinear optics
A nonlinear optical crystal having a chemical formula of Y i La j Al k B 16 O 48 , where 2.8≦i≦3.2, 0.8≦j≦1.2, i and j sum to about four, and k is about 12 is provided. The nonlinear optical crystal is useful for nonlinear optical applications including frequency conversion. Nonlinear optical crystals in a specific embodiment are characterized by UV blocking materials (e.g., some transition metals and lanthanides) at concentrations of less than 1,000 parts per million, providing high transmittance over portions of the UV spectrum (e.g., 175-360 nm).
1. A method of growing one or more nonlinear crystals of a composition, the method comprising:
providing a set of constituent components of the composition including an yttrium source, a lanthanum source, a boron source, and an aluminum source;
mixing the set of constituent components of the composition to form a component mixture;
heating the component mixture to a predetermined temperature, thereby forming a resultant melt;
cooling the resultant melt; and
forming the one or more nonlinear crystals of the composition as a precipitate from the resultant melt, wherein the one or more nonlinear crystals have a chemical formula of Y i La j Al k B 16 O 48 , where 2.0≦i≦3.6, 0.4≦j≦2.0, i and j sum to about four, and k is about 12.
2. The method of claim 1 wherein the yttrium source comprises yttrium oxide, the lanthanum source comprises lanthanum oxide, and the aluminum source comprises aluminum oxide.
3. The method of claim 1 wherein the boron source comprises at least one of boron oxide or boric acid.
4. The method of claim 3 wherein the one or more nonlinear crystals are characterized by an optical transmittance of greater than 0.7 at 250 nm.
5. The method of claim 4 wherein the optical transmittance is greater than 0.7 at 200 nm.
6. The method of claim 1 wherein a concentration of at least one or more of elements 22-30, 40-48, and 72-80 in the one or more nonlinear crystals is less than 1,000 parts per million.
7. The method of claim 1 wherein a concentration of molybdenum in the one or more nonlinear crystals is less than 50 parts per million.
8. The method of claim 1 wherein a concentration of at least one or more of elements 58-70 in the one or more nonlinear crystals is less than 1,000 parts per million.
9. The method of claim 1 wherein cooling the resultant melt is performed at a temperature rate of less than 20° K/hour.
10. The method of claim 1 wherein the one or more nonlinear crystals are characterized by a volume between about 1.0 mm 3 and about 10 cm 3 .