Process for producing high etch gains for electrolytic capacitor manufacturing
Anode foil, preferably aluminum anode foil, is etched using a process of treating the foil in an electrolyte bath composition comprising a sulfate and a halide, such as sodium chloride. The anode foil is etched in the electrolyte bath composition by passing a charge through the bath. The etched anode foil is suitable for use in an electrolytic capacitor.
1. An aqueous electrolyte bath composition for etching anode foil comprising:
about 0.5 percent to about 20 percent by weight surface-active, viscosity-modifying agent;
about 700 to about 2000 ppm sulfate, wherein the sulfate is selected from the group consisting of sodium sulfate, potassium sulfate, and lithium sulfate, and mixtures thereof;
about 2 percent to about 12 percent by weight sodium perchlorate; and
about 1 percent to about 6 percent by weight halide, wherein the temperature of said electrolyte bath is about 60° C. to about 95° C.
2. The electrolyte bath composition of claim 1 wherein the weight ratio of halide to sodium perchlorate is at about 2 to 1.
3. The electrolyte bath composition of claim 1 , comprising sodium perchlorate in an amount ranging from about 2 percent to about 6 percent; and a halide in an amount ranging from about 1 percent to about 3 percent, wherein the halide is sodium chloride.
4. The electrolyte bath composition of claim 1 , wherein the surface-active, viscosity-modifying agent comprises glycerin.
5. The electrolyte bath composition of claim 1 , wherein the electrolyte bath composition has a temperature ranging from about 75° C. to about 85° C.
6. The electrolyte bath composition of claim 1 , wherein the sulfate is sodium sulfate.
7. The electrolyte bath composition claim 1 , wherein the electrolyte bath further comprises sodium chloride in an amount ranging from about 1 percent to about 6 percent by weight composition and wherein the electrolyte bath comprises sodium perchlorate in an amount ranging from about 2 percent to about 12 percent by weight.
8. An aqueous electrolyte bath composition for etching anode foil comprising:
about 0.5 percent to about 20 percent by weight surface-active, viscosity-modifying agent;
an amount greater than 500 ppm to about 700 ppm sulfate, wherein the sulfate is selected from the group consisting of sodium sulfate, potassium sulfate, and lithium sulfate, and mixtures thereof;
about 2 percent to about 12 percent by weight sodium perchlorate; and
about 1 percent to about 6 percent by weight halide, wherein the temperature of said electrolyte bath is about 60° C. to about 95° C.
9. The electrolyte bath composition of claim 8 wherein the weight ratio of halide to sodium perchlorate is at about 2 to 1.
10. The electrolyte bath composition of claim 8 , comprising sodium perchlorate in an amount ranging from about 2 percent to about 6 percent; and a halide in an amount ranging from about 1 percent to about 3 percent, wherein the halide is sodium chloride.
11. The electrolyte bath composition of claim 8 , wherein the surface-active, viscosity-modifying agent comprises glycerin.
12. The electrolyte bath composition of claim 8 , wherein the electrolyte bath composition has a temperature ranging from about 75° C. to about 85° C.
13. The electrolyte bath composition of claim 8 , wherein the sulfate is sodium sulfate.
14. The electrolyte bath composition claim 8 , wherein the electrolyte bath further comprises sodium chloride in an amount ranging from about 1 percent to about 6 percent by weight composition and wherein the electrolyte bath comprises sodium perchlorate in an amount ranging from about 2 percent to about 12 percent by weight.