Burn rate sensitization of solid propellants using a nano-titania additive
View Patent ↗Adding nanoparticles as a catalyst to solid propellant fuel to increase and enhance burn rates of the fuel by up to 10 times or more and/or modifying the pressure index. A preferred embodiment uses TiO 2 nanoparticles mixed with a solid propellant fuel, where the nanoparticles are approximately 2% or less of total propellant mixture. The high surface to volume ratio of the nanoparticles improve the performance of the solid propellant fuel.
1. A composite solid propellant having a catalyst, consisting essentially of:
a composite solid propellant fuel; and
uncoated nanoparticles of TiO 2 additive consisting of nano-sized arrays of particles are mixed with the solid propellant fuel to produce a final propellant mixture having 0.4% of nanoparticles of TiO 2 consisting of nano-sized arrays of particles with a diameter of 10 nanometers or less, wherein the uncoated nanoparticles of TiO 2 act as the catalyst to increase the burn rate of the composite solid propellant for enhancing solid propellant burn rates that do not exhibit bi-plateau burning behaviors.
2. The composite solid propellant having the catalyst of claim 1 , wherein the composite solid propellant fuel consists of:
Ammonium Perchlorate (AP) and HTPB binder if nonmetallized, and AP, HTPB, Aluminum fuel, and Fe2O3 catalyst if metallized.
3. The solid propellant having the catalyst of claim 1 , wherein the materials for the synthesis of the TiO 2 nanoparticles includes Isopropanol anhydrous, 2,4-Pentanedione, and Titanium isopropoxide.
4. A composite solid propellant having a catalyst consisting essentially of
a composite solid propellant fuel; and
uncoated nanoparticles of TiO 2 additive consisting of nano-sized arrays of particles with a diameter of 10 nanometers or less mixed with the solid propellant fuel wherein the TiO 2 nanoparticles comprise:
Isopropanol anhydrous mixed with 2,4-Pentanedione to produce a first mixed solution;
a titanium Isoproproxide mixed with the first mixed solution to produce a second mixed solution; and
a deionized water mixed with the second mixed solution for hydrolysis to produce a final mixture, wherein the final mixture is aged to produce approximately 1.6 gram of nanoparticles of TiO 2 additive for enhancing solid propellant burn rates that are not bi-plateau burning behaviors.
5. The composite of claim 4 wherein the first mixed solution comprises:
approximately 100 ml of Isopropanol anhydrous; and
approximately 2 ml of 2,4-Pentanedione mixed together by stirring for approximately 20 minutes.
6. The composite of claim 1 , wherein mass percentage of the additive is between 0.4 to 2% of total propellant mass.
7. The composite of claim 4 , wherein mass percentage of the additive is between 0.4 to 2% of total propellant mass.