Graphite material, carbon material for battery electrode, and battery
View Patent ↗A graphite material is provided wherein D50% is 2 to 9 μm in particle diameter distribution based on volume as measured by laser diffraction, a specific surface area is 2 to 6 m 2 /g and no coating layer is substantially included in a surface of the particle. Also provided is a graphite material comprising substantially single-composition particles having an isotropic crystal structure, wherein D50% is 2 to 9 μm in particle diameter distribution based on volume as measured by laser diffraction, and a specific surface area is 2 to 6 m 2 /g.
1. A graphite material, said graphite material having a D50% of 2 to 9 μm in particle diameter distribution based on volume as measured by laser diffraction, a specific surface area of 2 to 6 m 2 /g; said material additionally containing no coating layer included in a surface of the particle, or containing no boundary between the surface layer and the inner layer of the material.
2. A graphite material having an isotropic crystal structure, wherein said graphite material has a D50% of 2 to 9 μm in particle diameter distribution based on volume as measured by laser diffraction, and a specific surface area is 2 to 6 m 2 /g.
3. The graphite material according to claim 1 , wherein the graphite material is produced from a raw material that is a non-needle coke.
4. The graphite material according to claim 3 , wherein the non-needle coke is a petroleum-derived pitch coke.
5. The graphite material according to claim 1 , wherein the graphite material has a laser Raman R value of no less than 0.01 and no more than 0.2, and a CTE at temperatures of 30 to 100° C. of no less than 4.0 ×10 −6 /°C. and no more than 5.0 ×10 −6 /°C.
6. The graphite material according to claim 1 , wherein the graphite material has a d 002 of 0.3362 nm to 0.3370 nm.
7. The graphite material according to claim 1 , wherein the graphite material contains primary particles and an aspect ratio of a primary particle is 1.00 to 1.32.
8. The graphite material according to claim 1 , wherein the graphite material has a loose bulk density of no less than 0.4 g/cm 3 , and a powder density of no less than 0.5 g/cm 3 and no more than 1 g/cm 3 after tapping is performed 400 times.