R-T-Cu-Mn-B type sintered magnet
An R-T-Cu—Mn—B based sintered magnet includes: 12.0 at % to 15.0 at % of R, which is at least one of the rare-earth elements that include Y and of which at least 50 at % is Pr and/or Nd; 5.5 at % to 6.5 at % of B; 0.08 at % to 0.35 at % of Cu; 0.04 at % to less than 0.2 at % of Mn; at most 2 at % (including 0 at %) of M, which is one, two, or more elements that are selected from the group consisting of Al, Ti, V, Cr, Ni, Zn, Ga, Zr, Nb, Mo, Ag, In, Sn, Hf, Ta, W, Au, Pb and Bi; and T as the balance, which is either Fe alone or Fe and Co and of which at most 20 at % is Co if T includes both Fe and Co.
1. An R-T-Cu—Mn—B based sintered magnet comprising:
12.0 at % to 15.0 at % of R, which is at least one of the rare-earth elements that include Y and of which at least 50 at % is Pr and/or Nd;
5.5 at % to 6.5 at % of B;
0.08 at % to 0.35 at % of Cu;
0.04 at % to less than 0.15 at % of Mn;
at most 2 at % (including 0 at %) of M, which is one, two, or more elements that are selected from the group consisting of Al, Ti, V, Cr, Ni, Zn, Ga, Zr, Nb, Mo, Ag, In, Sn, Hf, Ta, W, Au, Pb and Bi; and
T as the balance, which is either Fe alone or Fe and Co and of which at most 20 at % is Co if T includes both Fe and Co.
2. The R-T-Cu—Mn—B based sintered magnet of claim 1 , wherein the main phase of the magnet is an R 2 T 14 B type compound.
3. The R-T-Cu—Mn—B based sintered magnet of claim 2 , wherein the crystal grain size of the main phase is represented by an equivalent circle diameter of 12 μm or less.
4. The R-T-Cu—Mn—B based sintered magnet of claim 2 , wherein the combined area of portions of the main phase, of which the crystal grain sizes are represented by equivalent circle diameters of 8 μm or less, accounts for at least 70% of the overall area of the main phase.
5. The R-T-Cu—Mn—B based sintered magnet of claim 2 , wherein the combined area of portions of the main phase, of which the crystal grain sizes are represented by equivalent circle diameters of 5 μm or less, accounts for at least 80% of the overall area of the main phase.
6. The R-T-Cu—Mn—B based sintered magnet of claim 3 , wherein the combined area of portions of the main phase, of which the crystal grain sizes are represented by equivalent circle diameters of 8 μm or less, accounts for at least 70% of the overall area of the main phase.
7. The R-T-Cu—Mn—B based sintered magnet of claim 3 , wherein the combined area of portions of the main phase, of which the crystal grain sizes are represented by equivalent circle diameters of 5 μm or less, accounts for at least 80% of the overall area of the main phase.