Polyacetal resin composition, process for producing the same, and sliding member molded from the resin composition
View Patent ↗A polyacetal resin composition which has improved friction-wear characteristics as compared with conventional polyacetal resin compositions and which is less restricted in counter sliding members and can conform to a wide range of friction-wear conditions. A polyacetal resin composition comprising 100 parts by weight of (A) a polyacetal resin, 0.1 to 10 parts by weight of (B) a polyethylene wax having a number average molecular weight of 500 to 15,000, 0.1 to 10 parts by weight of (C) a polyethylene resin having a number average molecular weight of 2×10 4 to 50×10 4 , and 0.1 to 5 parts by weight of (D) a silicone oil having a kinetic viscosity at 25° C. of 50×10 4 cSt or more.
1. A process for producing a polyacetal resin composition comprising 100 parts by weight of (A) a polyacetal resin, 0.1 to 10 parts by weight of (B) a polyethylene wax having a number average molecular weight of 500 to 15,000, 0.1 to 10 parts by weight of (C) a polyethylene resin having a number average molecular weight of 2×10 4 to 50×10 4 , and 0.1 to 5 parts by weight of (D) a silicone oil having a kinetic viscosity at 25° C. of 50×10 4 cSt or more, the process comprising mixing a dispersion prepared by dispersing the silicone oil (D) into the polyethylene resin (C) with other components and melt kneading them together.
2. The process for producing a polyacetal resin composition according to claim 1 , wherein the [C]/[D] weight ratio of the polyethylene resin (C) to the silicone oil (D) when the polyethylene resin (C) dispersion of the silicone oil (D) is to be obtained is 30/70 to 75/25 and the [(B)/((C)+(D))] weight ratio of the polyethylene wax (B) to the total of the polyethylene resin (C) and the silicone oil (D) is 0.01 to 4.
3. A polyacetal resin composition comprising 100 parts by weight of (A) a polyacetal resin, 0.1 to 10 parts by weight of (B) a polyethylene wax having a number average molecular weight of 500 to 15,000, 0.1 to 10 parts by weight of (C) a polyethylene resin having a number average molecular weight of 2×10 4 to 50×10 4 , and 0.1 to 5 parts by weight of (D) a silicone oil having a kinetic viscosity at 25° C. of 50×10 4 cSt or more, the resin composition made by the steps of
mixing and kneading the polyethylene resin (C) and silicone oil (D) to obtain a dispersion composition of the silicone oil (D) dispersed into the polyethylene resin (C), and
subsequently mixing and kneading the dispersion composition with the polyacetal resin (A) and the polyethylene wax (B).
4. The polyacetal resin of claim 3 , wherein the polyethylene resin (C) is at least one selected from a low-density polyethylene having a density of 0.910 to 0.940 g/cm 3 , a linear low-density polyethylene having a density of 0.910 to 0.940 g/cm 3 obtained by copolymerizing ethylene with an α-olefin, and a super low-density polyethylene having a density of 0.875 g/cm 3 or more and less than 0.910 g/cm 3 .