Method of manufacturing ceramic/metal composite structure

1. A method of manufacturing a ceramic/metal composite structure, the method comprising the steps of:

providing a ceramic substrate;

forming a metal interface layer on the ceramic substrate;

placing a copper sheet on the metal interface layer, wherein multiple stages of pre-oxidizing processes are performed on the copper sheet before the copper sheet is placed on the metal interface layer, and the multiple stages of pre-oxidizing processes are performed at different temperatures and in different atmospheres with different oxygen partial pressures; and

heating the ceramic substrate, the metal interface layer and the copper sheet so that the metal interface layer forms strong bonds with the ceramic substrate and the copper sheet, wherein the metal interface layer provides a wetting effect for the copper sheet to the ceramic substrate at a high temperature so that the copper sheet wets a surface of the aluminum oxide.

2. The method according to claim 1 , wherein the metal interface layer is formed on the ceramic substrate by way of electroless plating.

3. The method according to claim 1 , wherein the multiple stages of pre-oxidizing processes are performed at a temperature ranging from 50 to 700° C.

4. The method according to claim 1 , wherein a coefficient of thermal expansion of the metal interface layer ranges between coefficients of thermal expansion of the ceramic substrate and the copper sheet.

5. The method according to claim 1 , wherein a coefficient of thermal expansion of the metal interface layer is smaller than or equal to a coefficient of thermal expansion of the copper sheet.

6. The method according to claim 1 , wherein a coefficient of thermal expansion of the metal interface layer is greater than or equal to a coefficient of thermal expansion of the copper sheet.

7. The method according to claim 1 , wherein a material of the metal interface layer is selected from the group consisting of gold, beryllium, bismuth, cobalt, copper, iron, nickel, palladium, platinum, titanium, yttrium and alloys thereof.

8. The method according to claim 1 , wherein a material of the metal interface layer is selected from the group consisting of nickel, a nickel alloy, copper and a copper alloy.

9. The method according to claim 1 , wherein the ceramic substrate, the metal interface layer and the copper sheet are heated to a temperature higher than 1000° C. to form the strong bonds.

10. The method according to claim 1 , wherein the ceramic substrate is composed of aluminum oxide.