Zirconia-mullite refractory raw material and a plate brick
Provided is a zirconia-mullite refractory raw material which is less likely to undergo alternation and microstructural degradation under high-temperature conditions, and low in thermal expansion rate, so as to have thermal shock resistance and corrosion resistance. The zirconia-mullite refractory raw material comprises crystalline zirconia and mullite as primary components, with the remainder being corundum and/or a matrix glass, wherein the crystalline zirconia includes a eutectic zirconia crystal having a grain size of 1.0 μm or less, and has a maximum grain size of 30 μm or less, and the matrix glass is contained in an amount of 5 mass % or less. The zirconia-mullite refractory raw material has a chemical composition comprising 30 to 55 mass % of ZrO 2 , 30 to 55 mass % of Al 2 O 3 and 10 to 25 mass % of SiO 2 , wherein each of the chemical components falls within a primary phase region of ZrO 2 in an Al 2 O 3 —ZrO 2 —SiO 2 system phase diagram.
1. A zirconia-mullite refractory raw material which is obtained through a fusion process, the zirconia-mullite refractory raw material comprising crystalline zirconia and mullite as primary components, with the remainder being corundum and/or a matrix glass, wherein the crystalline zirconia includes a eutectic zirconia crystal having a grain size of 1.0 μm or less, and the matrix glass is contained in an amount of 5 mass % or less.
2. A zirconia-mullite refractory raw material which is obtained through a fusion process, the zirconia-mullite refractory raw material consisting of crystalline zirconia and mullite, wherein the crystalline zirconia includes a eutectic zirconia crystal having a grain size of 1.0 μm or less.
3. The zirconia-mullite refractory raw material as defined in claim 1 , wherein the crystalline zirconia has a maximum grain size of 30 μm or less.
4. The zirconia-mullite refractory raw material as defined in claim 3 , which has a chemical composition comprising 30 to 55 mass % of ZrO 2 , 30 to 55 mass % of Al 2 O 3 and 10 to 25 mass % of SiO 2 , wherein each of the chemical components falls within a primary phase region of ZrO 2 in an Al 2 O 3 —ZrO 2 —SiO 2 system phase diagram.
5. The zirconia-mullite refractory raw material as defined in claim 4 , which has an apparent porosity of 3.0% or less.
6. The zirconia-mullite refractory raw material as defined in claim 5 , which contains Na 2 O, K 2 O, CaO, MgO, P 2 O 5 , B 2 O 3 , Fe 2 O 3 and MnO 2 in a total amount of 1.0 mass % or less.
7. A plate brick which contains the zirconia-mullite refractory raw material as defined in claim 1 , in an amount of 5 to 40 mass %.
8. The zirconia-mullite refractory raw material as defined in claim 2 , wherein the crystalline zirconia has a maximum grain size of 30 μm or less.
9. The zirconia-mullite refractory raw material as defined in claim 8 , which has a chemical composition comprising 30 to 55 mass % of ZrO 2 , 30 to 55 mass % of Al 2 O 3 and 10 to 25 mass % of SiO 2 , wherein each of the chemical components falls within a primary phase region of ZrO 2 in an Al 2 O 3 —ZrO 2 —SiO 2 system phase diagram.
10. The zirconia-mullite refractory raw material as defined in claim 9 , which has an apparent porosity of 3.0% or less.
11. The zirconia-mullite refractory raw material as defined in claim 10 , which contains Na 2 O, K 2 O, CaO, MgO, P 2 O 5 , B 2 O 3 , Fe 2 O 3 and MnO 2 in a total amount of 1.0 mass % or less.
12. A plate brick which contains the zirconia-mullite refractory raw material as defined in claim 2 , in an amount of 5 to 40 mass %.