Sheet-like optical member, resin composition for optical sheet, optical sheet and method for producing the same
A sheet-like optical member being difficult to damage a shape of a lens part. The sheet-like optical member includes: a substrate; and a lens part, which is formed on the substrate, is made of an active energy ray-curable resin, and has a plurality of unit prisms. The maximum logarithmic attenuation rate ΔE of the lens part measured by a rigid body pendulum method is 0.4 or less.
1. A sheet-like optical member comprising: a substrate; and a lens part, which is formed on the substrate, is made of an active energy ray-curable resin, and has a plurality of unit prisms,
wherein a maximum logarithmic attenuation rate ΔE of the lens pail measured by a rigid body pendulum method is 0.4 or less.
2. The sheet-like optical member according to claim 1 , wherein a maximum temperature of a logarithmic attenuation rate of the lens part measured by a rigid body pendulum method is 60° C. or more.
3. The sheet-like optical member according to claim 1 , wherein a refractive index of the lens part is 1.5 or more.
4. A sheet-like optical member comprising: a substrate; and a lens part, which is formed on the substrate, is made of an active energy ray-curable resin, and has a plurality of unit prisms,
wherein a tangent of loss elastic modulus and storage elastic modulus (tan θ=loss elastic modulus/storage elastic modulus) of the active energy ray-curable resin is 0.2 or less in a temperature range from 0° C. to 200° C.
5. The sheet-like optical member according to claim 4 , wherein an equilibrium elastic modulus (160° C., 1 Hz) of the active energy ray-curable resin is 1.0×10 8 Pa or more.
6. The sheet-like optical member according to claim 4 , wherein a refractive index of the lens part is 1.5 or more.
7. An optical sheet comprising: a transparent substrate; and
a lens part, which is made of a number of unit prisms, formed from an active energy ray-curable resin composition, and formed on the transparent substrate, wherein, in the lens part, a difference between an overall transmittance after a load of 26 kg/cm 2 is applied to a pinnacle of the unit prism for 24 hours under an environment of 40° C. and an overall transmittance before the load is applied is 10% or less.
8. The optical sheet according to claim 7 , wherein: Tg of the lens part measured with a rigid body pendulum is 80° C. or more and 160° C. or less, Tg (1 Hz) of the lens part measured by a dynamic viscoelastic measurement is 80° C. or more and 160° C. or less, and an equilibrium elastic modulus (160° C., 1 Hz) of the lens part measured by a dynamic viscoelastic measurement is 3×10 7 Pa or more and 1×10 8 Pa or less.
9. The optical sheet according to claim 7 , wherein a refractive index of the lens part is 1.555 or more and 1.600 or less.
10. A resin composition for an optical sheet for forming a lens part made of a number of unit prisms provided to an optical sheet, wherein a cured material of the resin composition has a difference of 10% or less between an overall transmittance after a load of 26 kg/cm 2 is applied for 24 hours under an environment of 40° C. and an overall transmittance before the load is applied.
11. The resin composition for an optical sheet according to claim 10 , wherein a refractive index of the cured resin composition is 1.555 or more and 1.600 or less.
12. The resin composition for an optical sheet according to claim 10 , wherein the resin composition comprises: bisphenol A epoxy(meth)acrylate; urethane (meth)acrylate which is a reaction product of tolylenediisocyanate and/or xylylene diisocyanate, a diol compound represented by a formula (1), and OH-containing (meth)acrylate represented by a formula (2); one kind or two or more kinds of monofunctional monomer selected from a phenoxyethyl (meth)acrylate derivative represented by a formula (3), acryloylmorpholine, isobomyl (meth)acrylate, and benzyl (meth)acrylate; one kind or two or more kinds of polyfunctional monomer selected from an isocyanulate (meth)acrylate derivative represented by a formula (4), dipentaerythritol hexa(meth)acrylate, trimethylolpropane tri(meth)acrylate, glycerin tri(meth)acrylate, and pentaerythritol tri(meth)acrylate; and a photoinitiator,
13. A method for producing an optical sheet having a lens part which has a number of unit prisms on a transparent substrate, comprising at least a step for: forming a lens part wherein an active energy ray is irradiated after the resin composition for an optical sheet according to claim 10 is coated on a shaping mold to form the lens part.
14. The method for producing an optical sheet according to claim 13 , wherein the lens part formed by the step for forming a lens part has: Tg measured with a rigid body pendulum in the range of 80° C. or more and 160° C. or less, Tg (1 Hz) measured by a dynamic viscoelastic measurement in the range of 80° C. or more and 160° C. or less, and an equilibrium elastic modulus (160° C., 1 Hz) measured by a dynamic viscoelastic measurement in the range of 3×10 7 Pa or more and 1×10 8 Pa or less.