Method of producing aqueous resin composition
A polyolefin wax-containing aqueous resin composition that can provide excellent properties without the use of a surfactant is provided. The aqueous resin composition is obtained by heating and dissolving 100 parts by mass of a carboxyl group-containing polyolefin wax in the presence of 15 to 67 parts by mass of a compound that satisfies formula (1) shown below, and 90 to 380 parts by mass of water, and then dispersing this with a basic compound that has been added at a ratio of 1 to 4 chemical equivalents per carboxyl group of the carboxyl group-containing polyolefin wax. C m H 2m+1 —(OCH 2 CH 2 ) n —OH Formula (1) m: an integer from 4 to 6, n: an integer from 1 to 4.
1. A method of producing an aqueous resin composition consisting of the following steps:
heating and dissolving 100 parts by mass of a carboxyl group-containing polyolefin wax in the presence of 15 to 67 parts by mass of a compound that satisfies Formula (1) below, and 90 to 380 parts by mass of water to provide an aqueous medium, dispersing the wax in the aqueous medium by adding a basic compound at a ratio of 1 to 4 basic group equivalents per carboxyl group of the carboxyl group-containing polyolefin wax and then mixing:
C m H 2m+1 —(OCH 2 CH 2 ) n —OH Formula (1)
m: an integer from 4 to 6, n: an integer from 1 to 4.
2. The method of claim 1 , wherein the step of heating and dissolving the polyolefin wax comprises heating at a temperature in the range of from 100 to 160 degrees Celsius.
3. The method of claim 1 , wherein the step of dispersing by adding a basic compound comprises heating at a temperature in the range of from 90 to 160 degrees Celsius.
4. The method of claim 1 , wherein the polyolefin wax and water are combined in a ratio of one to two.
5. The method of claim 1 , wherein the compound that satisfies Formula (1) is added in an amount of between 15 to 22.5 parts by mass.
6. The method of claim 1 , wherein the compound that satisfies Formula (1) is selected from the group consisting of ethylene glycol mono-n-butyl ether, diethylene glycol mono-n-butyl ether and ethylene glycol mono-n-ethylhexyl ether.
7. The method of claim 1 , wherein the carboxyl group-containing polyolefin wax is an acid-modified polyolefin wax which has an acid value of 10 to 110 mgKOH/g and is obtained by graft-copolymerization of at least one species selected from the group consisting of α,β-unsaturated carboxylic acids and anhydrides thereof with a polyolefin wax.
8. The method of claim 1 , wherein the carboxyl group-containing polyolefin wax has an acid value of 10 to 110 mgKOH/g through oxidation treatment of a polyolefin wax.
9. The method of claim 1 , wherein the carboxyl group-containing polyolefin wax has a melt viscosity at 170° C. of not more than 30,000 m Pas.