Glass-tube extended-baking process
Disclosed is a method of heat treating quartz glass deposition tubes at between 900° C. and 1200° C. for at least 115 hours. The resulting deposition tubes are useful in forming optical preforms that can yield optical fibers having reduced added loss.
1. An extended-baking method for improving the optical properties of a glass deposition tube, comprising the step of subjecting the glass deposition tube to heat-treatment at 900° C. or higher under reduced pressure of 100 millitorr or less for at least 115 hours.
2. A method according to claim 1 , wherein the step of subjecting the glass deposition tube to heat-treatment comprises subjecting the glass deposition tube to heat-treatment of between about 1000° C. and 1200° C. for about 150 hours or more.
3. A method according to claim 1 , wherein the step of subjecting the glass deposition tube to heat-treatment comprises subjecting the glass deposition tube to heat-treatment under reduced pressure of between about 1 millitorr and 50 millitorr.
4. A method according to claim 1 , wherein the step of subjecting the glass deposition tube to heat-treatment comprises subjecting the glass deposition tube to heat-treatment in an inert-gas environment.
5. A method according to claim 1 , wherein the glass deposition tube possesses less than 100 ppm halogen.
6. A method according to claim 1 , further comprising:
depositing a glass inner cladding layer and a glass core layer, respectively, into the interior of the heat-treated glass deposition tube; and
collapsing the heat-treated glass deposition tube to yield an optical preform.
7. A method for improving the optical properties of a glass tube via extended-baking heat treatment, comprising the step of subjecting the glass tube to heat-treatment at 900° C. or higher for at least 125 hours.
8. A method according to claim 7 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting the glass tube to heat-treatment in an inert-gas environment.
9. A method according to claim 7 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting the glass tube to heat-treatment in an environment that is substantially free of hydrogen and/or hydrogen-bearing species.
10. A method according to claim 7 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting a jacket tube to heat-treatment under reduced pressure of 75 millitorr or less.
11. A method according to claim 7 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting a jacket tube to heat-treatment under reduced pressure of 50 millitorr or less for at least 150 hours.
12. A method according to claim 7 , wherein the glass tube possesses less than 100 ppm halogen.
13. A method according to claim 7 , wherein the glass tube possesses less than 100 ppb iron and less than 100 ppm aluminum.
14. A method according to claim 7 , further comprising:
incorporating the heat-treated glass tube into an optical preform; and
drawing an optical fiber from the optical preform.
15. A method for improving the optical properties of a glass tube via extended-baking heat treatment, comprising the step of subjecting the glass tube to heat-treatment at about 1000° C. or higher under reduced pressure of between about 1 millitorr and 100 millitorr for at least 115 hours.
16. A method according to claim 15 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting a cladding tube to heat-treatment for at least 125 hours in an inert-gas environment.
17. A method according to claim 15 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting a cladding tube to heat-treatment for at least 200 hours.
18. A method according to claim 15 , wherein the step of subjecting the glass tube to heat-treatment comprises subjecting the glass tube to heat-treatment under reduced pressure of between 1 millitorr and 50 millitorr for at least 400 hours.
19. A method according to claim 15 , wherein the glass tube possesses less than 10 ppm halogen.
20. A method according to claim 15 , further comprising:
incorporating the heat-treated glass tube into an optical preform; and
drawing an optical fiber from the optical preform.