Primer composition, waterproof floor slab structure using the same, and method for waterproofing floor slab
A primer composition used for applying a radical-curable resin-based waterproof material onto a concrete floor slab of an existing or newly established road bridge, is a troublesome application. For example, it is a problem in that a large machine is required for application thereof. The primer composition is a resin composition containing a urethane (meth)acrylate resin, (B) a polymerizable unsaturated monomer containing a hydroxyalkyl (meth)acrylate (B-1) and another polymerizable unsaturated monomer (B-2), (C) a curing accelerator, (D) a paraffin wax, and (E) a drying aid, in which the above components satisfy a specific molar ratio and specific mass ratios. The primer composition has a good crack-load-following capability, blistering resistance, adhesiveness, and bending resistance. Also provided is a waterproof floor slab structure using the primer composition and a method for waterproofing a floor slab.
1. A primer composition for application to concrete, the primer composition comprising a resin composition containing (A) a urethane (meth)acrylate resin (A-1) obtained by reacting a hydroxyalkyl (meth)acrylate (A-1-3) with a terminal-isocyanate-group-containing urethane prepolymer obtained by reacting polytetramethylene glycol (A-1-1) having a number-average molecular weight of 650 to 2,000 with a polyisocyanate component (A-1-2), or a mixture of the urethane (meth)acrylate resin (A-1) and a urethane (meth)acrylate resin (A-2) obtained by reacting a hydroxyalkyl (meth)acrylate (A-2-3) with a terminal-isocyanate-group-containing urethane prepolymer obtained by reacting a polyether polyol (A-2-1) selected from polyoxypropylene diol and polyoxyethylene diol and having a number-average molecular weight of 650 to 2,000 with a polyisocyanate component (A-2-2);
(B) a polymerizable unsaturated monomer containing a hydroxyalkyl (meth)acrylate (B-1) and a polymerizable unsaturated monomer (B-2) other than the (A-1), the (A-2), and the (B-1); (C) a curing accelerator; (D) a paraffin wax; and (E) a cobalt organic acid salt, wherein a molar ratio of the (B)/the (A) is 4 to 20, a mass ratio of the (A-1)/the (A-2) is 100/0 to 10/90, and a mass ratio of the (B-1)/the (B-2) is 35/65 to 5/95.
2. The primer composition for application to concrete according to claim 1 , wherein the hydroxyalkyl (meth)acrylates (A-1-3) and (A-2-3) are each 2-hydroxyethyl methacrylate.
3. The primer composition for application to concrete according to claim 1 , wherein the hydroxyalkyl (meth)acrylate (B-1) is 2-hydroxyethyl methacrylate.
4. The primer composition for application to concrete according to claim 1 , wherein the polymerizabie unsaturated monomer (B-2) other than the (B-1) is at least one selected from methyl methacrylate, phenoxyethyl methacrylate, and dicyclopentenyloxyethyl methacrylate.
5. The primer composition for application to concrete according to claim 1 , wherein the curing accelerator (C) is an amine compound.
6. A waterproof floor slab structure comprising at least, from the bottom, a floor slab; a layer composed of a cured product of the primer composition for application to concrete according to claim 1 ; a layer composed of a cured product of a radical-curable resin-based waterproof material for the floor slab; and an asphalt pavement layer, in that order.
7. A method for waterproofing a floor slab, comprising applying, onto a floor slab, the primer composition for application to concrete according to claim 1 ; subsequently applying a radical-curable resin-based waterproof material for the floor slab; and laying an asphalt paving material.