Cold shrinkable article including an epichlorohydrin composition
A composition includes an elastomeric composition. The elastomeric composition can include an epichlorohydrin composition, and the elastomeric composition can be substantially free of a fluoroelastomer composition. The composition can further include a filler material which includes a reinforcement-grade carbon black. The composition can further include a peroxide curative.
1. A tubular cold-shrinkable material comprising the reaction product of:
an elastomeric composition, the elastomeric composition comprising an epichlorohydrin composition, and the elastomeric composition being free of a fluoroelastomer composition;
a filler material, the filler material comprising one or both of a reinforcement-grade carbon black and a fumed silica; and
a peroxide curative, wherein the quantity of filler material is in the range of about 10 phr to about 25 phr and the quantity of peroxide curative is in the range of about 0.5 phr to about 4.0 phr.
2. The material as defined by claim 1 , wherein the reinforcement-grade carbon black comprises carbon black having an average particle size of less than about 40 nm.
3. The material as defined by claim 1 , wherein the fumed silica comprises a silane treated fumed silica.
4. The material as defined by claim 1 , wherein the material further comprises a cross-linking agent or cross-linking co-agent.
5. The material as defined by claim 1 , wherein the material exhibits an elongation greater than about 550% and a permanent set less than about 25% at room temperature.
6. The material as defined by claim 1 , wherein the material exhibits an elongation greater than about 300% and a permanent set less than about 25% at 130 degrees Celsius.
7. The material as defined by claim 1 , wherein the material exhibits an elongation greater than about 275% and a permanent set less than about 25% at 150 degrees Celsius.
8. The material as defined by claim 1 , wherein the material does not tear while being held for seven days in a 200% radially expanded state at 150 degrees Celsius.
9. The material defined by claim 1 , wherein the material exhibits less than about a 25% weight increase when immersed in diesel fuel for 24 hours at a temperature of about 49 degrees Celsius.
10. The material defined by claim 1 , wherein the material exhibits less than about a 10% weight increase when immersed in hydraulic fluid for 24 hours at a temperature of about 71 degrees Celsius.