Method of making a metal bellows assembly having an intermediate plate
The formation of a bellows made up of a stack of a predetermined number of ring-convolutions and having an intermediate plate supported within said stack is achieved by supplying several thin metal rings, each having inner and outer edges. A pair of these metal rings are positioned in contiguous relationship and their adjacent inside edges are welded together to form a ring-convolution. This process is repeated until a sufficient number of ring-convolutions are made to eventually make the desired bellows. Before these separate ring-convolutions are fused to each other, an intermediate plate and a support ring are made. The intermediate plate is a disc of metal that is sized smaller than the inside diameter of the rings and is secured to the support ring. The support ring is then positioned between two formed ring-convolutions in contiguous relationship and the three abutting outside edges are welded to each other to form a support plate convolution. The already made ring-convolutions and the support plate convolution are then stacked in the desired order and in contiguous relationship. All not-yet welded adjacent outside edges of said ring-convolutions and said support plate convolution are then welded to form the bellows. A bottom plate is formed and welded to the outside edge of the bottommost ring-convolution and a top ring is finally welded to the uppermost convolution to complete the bellows. The top ring is meant to be welded to a base plate of an infusion pump.
1. A method for forming a bellows made up of a stack of a predetermined number of ring-convolutions and having an intermediate plate supported within said stack, said method comprising the steps of:
a) supplying a plurality of metal rings, each ring having a first outer diameter defining a first outer edge and a first inner diameter, defining a first inner edge;
b) positioning a pair of said metal rings in contiguous relation to each other,
c) welding said first inner edges of said pair of metal rings to each other to form a ring-convolution;
d) repeating steps (a) through (c) until said predetermined number of ring-convolutions are made;
e) supplying a support ring, said support ring having a second outer diameter that is equal to said first outer diameter of said metal rings and adapted to hold an intermediate plate;
f) supplying said intermediate plate having a predetermined thickness and a third inside diameter that is less than said first inside diameter of said metal rings;
g) welding said intermediate plate to said support ring;
h) positioning said support ring between a pair of ring-convolutions in contiguous relation to each other;
i) welding said second outer edge of said support ring to said first outer edges of said respective adjacent ring-convolutions to form a support plate convolution;
j) positioning said ring-convolutions of (c) and said support plate convolution of step (i) in a prescribed stacked order in contiguous relation to each other; and
k) welding all not-yet welded adjacent outside edges of said ring-convolutions and said support plate convolution to form said bellows.
2. The method of claim 1 , wherein the welding steps (c), (i), and (k), are performed using a laser producing a high-energy output beam.
3. The method of claim 2 , wherein the welding steps are performed by:
holding said rings to be welded in a jig; and
moving said output beam of said laser with respect to said held rings so that the output beam contacts the rings and fuses them together at the point of contact.
4. The method of claim 2 , wherein the welding steps are performed by:
holding said rings to be welded in a rotatable jig; and
rotating said jig with respect to said output beam of said laser so that the output beam contacts the rings and fuses them together at the point of contact.
5. The method of claim 2 , wherein said laser pulses said output beam so that the resulting weld is formed by multiple small spot welds.
6. The method of claim 5 , wherein adjacent spot welds overlap each other by a predetermined amount.
7. The method of claim 6 , wherein said overlap is between 30% and 75%, measured in area.
8. The method of claim 1 , wherein the welding steps (c), (i), and (k) are performed using a TIG (Tungsten Inert Gas) welder.
9. The method of claim 8 , wherein the welding steps are performed by:
holding said rings to be welded in a jig; and
moving said TIG welder with respect to said held rings so that the heat energy of the TIG welder contacts the rings and fuses them together at the point of contact.
10. The method of claim 8 , wherein the welding steps are performed by:
holding said rings to be welded in a rotatable jig; and
rotating said jig with respect to said TIG welder so that the TIG welder contacts the rings and fuses them together at the point of contact.
11. The method of claim 1 , wherein said welding step (g) is performed using a electrical-current spot welder.
12. The method of claim 1 , wherein said rings and support plate are made from titanium metal.
13. The method of claim 1 , wherein said steps further include:
providing a bottom cover having an outer diameter which is equal to said first outer diameter of a ring;
positioning said bottom cover and said bottom ring-convolution of said stack in contiguous relationship, and
welding said adjacent outer edges of said ring-convolution and said bottom ring.
14. The method of claim 13 , wherein said bellows stack is further attached to a base plate of an implantable infusion pump and used as a fluid reservoir to hold a supply of liquid medication.
15. The method of claim 14 , wherein an attached step includes laser welding.
16. A method for forming a bellows made up of a stack of a predetermined number of ring-convolutions and having an intermediate plate supported within said stack, said method comprising the steps of:
a) supplying a plurality of metal rings, each ring having a first outer diameter defining a first outer edge and a first inner diameter, defining a first inner edge;
b) positioning a pair of said metal rings in contiguous relation to each other,
c) welding said first inner edges of said pair of metal rings to each other to form a ring-convolution;
d) repeating steps (a) through (c) until said predetermined number of ring-convolutions are made;
e) supplying a support ring, said support ring having a second outer diameter that is equal to said first outer diameter of said metal rings and adapted to hold said intermediate plate;
f) supplying an intermediate plate having a predetermined thickness and a third inside diameter that is less than said first inside diameter of said metal rings;
g) welding said intermediate plate to said support ring;
h) positioning said support ring between a pair of ring-convolutions in contiguous relation to each other;
i) welding said second outer edge of said support ring to said first outer edges of said respective adjacent ring-convolutions to form a support plate convolution;
j) positioning a pair of ring-convolutions of (c) in contiguous relation to each other;
k) welding said abutting outside edges of said pair of ring-convolutions to each other, forming a stack of connected convolutions;
l) positioning another ring-convolution to said stack of step (k), again in contiguous relation;
m) welding said outside edge of said added ring-convolution to said adjacent outside edge of an adjacent ring-convolution of said stack;
n) repeating steps (l) and (m), until said stack reaches a predetermined location of said support convolution within said stack;
o) positioning said support convolution onto said stack in contiguous relation; and
p) welding said adjacent outside edges of said added support convolution with said adjacent outside edge of an adjacent ring-convolution of said stack to complete said bellows.
17. The method of claim 16 , wherein the welding steps (c), (i), (k), (m), and (p) are performed using a laser producing a high-energy output beam.
18. The method of claim 17 , wherein the welding steps are performed by:
holding said rings to be welded in a jig; and
moving said output beam of said laser with respect to said held rings so that the output beam contacts the rings and fuses them together at the point of contact.
19. The method of claim 17 , wherein the welding steps are performed by:
holding said rings to be welded in a rotatable jig; and
rotating said jig with respect to said output beam of said laser so that the output beam contacts the rings and fuses them together at the point of contact.
20. The method of claim 17 , wherein said laser pulses said output beam so that the resulting weld is formed by multiple small spot welds.
21. The method of claim 20 , wherein adjacent spot welds overlap each other by a predetermined amount.
22. The method of claim 21 , wherein said overlap is between 30% and 75%, measured in area.
23. The method of claim 16 , wherein the welding steps (c), (i), (k), (m), and (p) are performed using a TIG (Tungsten Inert Gas) welder.
24. The method of claim 23 , wherein the welding steps are performed by:
holding said rings to be welded in a jig; and
moving said TIG welder with respect to said held rings so that the heat energy of the TIG welder contacts the rings and fuses them together at the point of contact.
25. The method of claim 23 , wherein the welding steps are performed by:
holding said rings to be welded in a rotatable jig; and
rotating said jig with respect to said TIG welder so that the TIG welder contacts the rings and fuses them together at the point of contact.
26. The method of claim 16 , wherein said welding step (g) is performed using a electrical-current spot welder.
27. The method of claim 16 , wherein said rings and support plate are made from titanium metal.
28. The method of claim 16 , wherein said steps further include:
providing a bottom cover having an outer diameter which is equal to said first outer diameter of a ring;
positioning said bottom cover and said bottom ring-convolution of said stack in contiguous relationship, and
welding said adjacent outer edges of said ring-convolution and said bottom ring.
29. The method of claim 28 , wherein said bellows stack is further attached to a base plate of an implantable infusion pump and used as a fluid reservoir to hold a supply of liquid medication.
30. The method of claim 29 , wherein an attached step includes laser welding.
31. The method of claim 1 , wherein the first outside diameter of all of the metal rings is the same.
32. The method of claim 1 , wherein the first inside diameter of all of the metal rings is the same.
33. The method of claim 31 , wherein the first inside diameter of all of the metal rings is the same.
34. The method of claim 16 , wherein the first outside diameter of all of the metal rings is the same.
35. The method of claim 16 , wherein the first inside diameter of all of the metal rings is the same.
36. The method of claim 34 , wherein the first inside diameter of all of the metal rings is the same.