Lead-free copper alloy for casting with excellent mechanical properties
Disclosed is a lead-free copper alloy for casting which contains 0.1-0.7% of S, 8% or less (excluding 0%) of Sn, and 6% or less (excluding 0%) of Zn, and in which a sulfide is dispersed and the average spheroidization ratio of the sulfide is 0.7 or greater. Due to this constitution, said lead-free copper alloy for casting has excellent mechanical properties such as strength, high pressure resistance and good machinability and, therefore, is useful as a starting material for faucet metal fittings, water faucet and so on, even though the alloy contains no lead which causes deterioration of water.
1. A lead free copper alloy for casting, consisting of:
0.1% to 0.7% (% means mass % in the case of component) of S,
8% or lower (not including 0%) of Sn, and
4% or lower (not including 0%) of Zn,
wherein the remaining percent is
copper, and
unavoidable impurities, and
wherein spherical sulfide with a spherical ratio of 0.7 or larger is dispersed in the lead free copper alloy.
2. The lead free copper alloy for casting of claim 1 , wherein the area fraction of copper sulfide in all sulfides in the alloy is 70% or larger.