Honeycomb structure
A honeycomb structure includes aluminum titanate, cell walls, and pore portions. The cell walls extend along a longitudinal direction of the honeycomb structure to define cells between the cell walls. The pore portions have an average pore diameter of about 10 μm to about 20 μm. A length of a longest pore portion among the pore portions in a binary image including substrate portions and the pore portions is about 8 times or less of the average pore diameter. The binary image is converted from a microscopic image of a cross section of the cell walls in parallel with the longitudinal direction. The length is measured along a line drawn in a direction perpendicular to a thickness direction of the cell walls.
1. A honeycomb structure comprising:
aluminum titanate;
cell walls extending along a longitudinal direction of the honeycomb structure to define cells between the cell walls;
pore portions having an average pore diameter of about 10 μm to about 20 μm; and
a length of a longest pore portion among the pore portions in a binary image comprising substrate portions and the pore portions being about 8 times or less of the average pore diameter, wherein the binary image is converted from a microscopic image of a cross section of the cell walls in parallel with the longitudinal direction, and wherein the length is measured along a line drawn in a direction perpendicular to a thickness direction of the cell walls, and
wherein the honeycomb structure is produced by using a mixture including a pore-forming agent having a particle-distribution index of 1.8-2.0, where the particle-distribution index is calculated as being equal to (D90-D10)/D50, where D90 is a 90% particle diameter, D50 is a 50% particle diameter, and D10 is a 10% particle diameter.
2. The honeycomb structure according to claim 1 ,
wherein the length of the longest pore portion is about 7 times or less of the average pore diameter.
3. The honeycomb structure according to claim 1 ,
wherein the length of the longest pore portion is about 5 times or less of the average pore diameter.
4. The honeycomb structure according to claim 1 ,
wherein a total volume of pores having a pore diameter within a range from (the average pore diameter−about 2 μm) to (the average pore diameter+about 2 μm) in a pore diameter distribution is about 60% or more of a whole pore volume.
5. The honeycomb structure according to claim 1 ,
wherein a total volume of pores having a pore diameter within a range from (the average pore diameter−about 2 μm) to (the average pore diameter+about 2 μm) in a pore diameter distribution is about 70% or more of a whole pore volume.
6. The honeycomb structure according to claim 1 ,
wherein a porosity of the honeycomb structure is from about 40% to about 50%.
7. The honeycomb structure according to claim 1 ,
wherein each of the cells is sealed at either one end.
8. The honeycomb structure according to claim 1 ,
wherein an aperture ratio of the honeycomb structure is from about 50% to about 75%.
9. The honeycomb structure according to claim 1 ,
wherein a thickness of the cell walls is from about 0.15 mm to about 0.4 mm.
10. The honeycomb structure according to claim 1 ,
wherein a catalyst is supported on the honeycomb structure.
11. The honeycomb structure according to claim 10 ,
wherein said catalyst comprises at least one of noble metal elements, alkaline metal elements, alkaline earth metal elements, and metal oxides.
12. The honeycomb structure according to claim 1 , wherein
the honeycomb structure is prepared by
mixing an additive with powders of Al 2 O 3 and TiO 2 to prepare a material powder,
sintering said material powder to manufacture a sintered body of aluminum titanate,
pulverizing and classifying said sintered body of aluminum titanate to prepare a coarse powder of aluminum titanate,
preparing another sintered body of aluminum titanate,
pulverizing and classifying said another sintered body of aluminum titanate at a different degree of pulverization and classification to prepare a fine powder of aluminum titanate,
preparing a mixture including said coarse powder of aluminum titanate and said fine powder of aluminum titanate,
extrusion-molding said mixture to manufacture a honeycomb molded body, and
firing said honeycomb molded body.
13. The honeycomb structure according to claim 12 ,
wherein said additive comprises at least one of MgO and alkaline feldspar.
14. The honeycomb structure according to claim 12 ,
wherein said mixture further comprises a pore-forming agent, an organic binder, a plasticizer, a lubricant, and water.
15. The honeycomb structure according to claim 12 , wherein
said coarse powder of aluminum titanate has an average particle diameter of from about 5.0 μm to about 50.0 μm, and said fine powder of aluminum titanate has an average particle diameter of from about 0.1 μm to about 3.0 μm.
16. The honeycomb structure according to claim 12 ,
wherein a mixing ratio of said coarse powder of aluminum titanate to said fine powder of aluminum titanate in said mixture is from about (9:1) to about (6:4).
17. A method for manufacturing a honeycomb structure, the method comprising:
molding a mixture to manufacture a honeycomb molded body having a plurality of cells longitudinally disposed substantially in parallel with one another; and
firing the honeycomb molded body to manufacture a honeycomb structure,
wherein the mixture comprises:
a pore-forming agent having a particle-distribution index of 1.8-2.0, where the particle-distribution index is calculated as being equal to (D90-D10)/D50, where D90 is a 90% particle diameter, D50 is a 50% particle diameter, and D10 is a 10% particle diameter, and
wherein the honeycomb structure has:
cell walls extending along a longitudinal direction of the honeycomb structure to define cells between the cell walls,
pore portions having an average pore diameter of about 10 μm to about 20 μm; and
a length of a longest pore portion among the pore portions in a binary image comprising substrate portions and the pore portions being about 8 times or less of the average pore diameter, wherein the binary image is converted from a microscopic image of a cross section of the cell walls in parallel with the longitudinal direction, and wherein the length is measured along a line drawn in a direction perpendicular to a thickness direction of the cell walls.
18. The method according to claim 17 ,
wherein the length of the longest pore portion is about 7 times or less of the average pore diameter.
19. The method according to claim 17 ,
wherein the length of the longest pore portion is about 5 times or less of the average pore diameter.
20. The method according to claim 17 ,
wherein a total volume of pores having a pore diameter within a range from (the average pore diameter−about 2 μm) to (the average pore diameter+about 2 μm) in a pore diameter distribution is about 60% or more of a whole pore volume.
21. The method according to claim 17 ,
wherein a total volume of pores having a pore diameter within a range from (the average pore diameter−about 2 μm) to (the average pore diameter+about 2 μm) in a pore diameter distribution is about 70% or more of a whole pore volume.
22. The method according to claim 17 ,
wherein a porosity of the honeycomb structure is from about 40% to about 50%.
23. The method according to claim 17 ,
wherein each of the cells is sealed at either one end.
24. The method according to claim 17 ,
wherein an aperture ratio of the honeycomb structure is from about 50% to about 75%.
25. The method according to claim 17 ,
wherein a thickness of the cell walls is from about 0.15 mm to about 0.4 mm.
26. The method according to claim 17 ,
wherein a catalyst is supported on the honeycomb structure.
27. The method according to claim 26 ,
wherein said catalyst comprises at least one of noble metal elements, alkaline metal elements, alkaline earth metal elements, and metal oxides.
28. The method according to claim 17 , wherein
the honeycomb structure is prepared by
mixing an additive with powders of Al 2 O 3 and TiO 2 to prepare a material powder,
sintering said material powder to manufacture a sintered body of aluminum titanate, pulverizing and classifying said sintered body of aluminum titanate to prepare a coarse powder of aluminum titanate,
preparing another sintered body of aluminum titanate,
pulverizing and classifying said another sintered body of aluminum titanate at a different degree of pulverization and classification to prepare a fine powder of aluminum titanate,
preparing a mixture including said coarse powder of aluminum titanate and said fine powder of aluminum titanate,
extrusion-molding said mixture to manufacture a honeycomb molded body, and
firing said honeycomb molded body.
29. The method according to claim 28 ,
wherein said additive comprises at least one of MgO and alkaline feldspar.
30. The method according to claim 28 ,
wherein said mixture further comprises a pore-forming agent, an organic binder, a plasticizer, a lubricant, and water.
31. The method according to claim 28 , wherein
said coarse powder of aluminum titanate has an average particle diameter of from about 5.0 μm to about 50.0 μm, and
said fine powder of aluminum titanate has an average particle diameter of from about 0.1 μm to about 3.0 μm.
32. The method according to claim 28 ,
wherein a mixing ratio of said coarse powder of aluminum titanate to said fine powder of aluminum titanate in said mixture is from about (9:1) to about (6:4).