Spring steel with excellent resistance to hydrogen embrittlement and steel wire and spring obtained from the steel

1. A spring steel, having a composition consisting essentially of:

C: 0.35-0.65%,

Si: 1.5-2.5%,

Mn: 0.05-1%,

Cr: 0.05-1.9%,

P: 0.015% or less (exclusive of 0%),

S: 0.015% or less (exclusive of 0%),

Ti: 0.0250.1%,

Al: 0.05% or less (exclusive of 0%),

N: 0.01% or less (exclusive of 0%),

Nb : 0.1% or less (exclusive of 0%);

optionally one or more of Cu, Ni, and V; and

a balance being Fe and inevitable impurities,

wherein said spring steel has a tensile strength of 2000 MPa or higher and a hydrogen embrittlement fatigue crack life of 712 sec. or higher, and an amount of Ti in Ti nitride, an amount of Ti in Ti sulfide, and an amount of Ti in Ti carbide satisfy following formulas (1), (2), and (3);

[Ti with N ]≧3.42×[N]−0.354×[Al]−0.103×[Nb]  (1)

[Ti with S ]≧1.49×[S]  (2)

[Ti with C ]≧0.015  (3),

in which [Ti with N ] represents the amount of Ti (mass %) forming Ti nitride, [Ti with S ] represents the amount of Ti (mass %) forming Ti sulfide, [Ti with C ] represents the amount of Ti (mass %) forming Ti carbide, and [N], [Al], [Nb], and [S] represent an amount (mass %) of each element in the steel; and the percentages above are mass percentages

and wherein the steel is produced by a process comprising:

cooling a steel having the composition within the range from 1,500° C. to 1,400° C. at a rate of 0.8° C./sec or less;

setting the heating temperature of the steel to at least 1,200° C. but no more that 1,300° C.;

spraying water on the hot steel before carrying out a hot-rolling process until the steel reaches a temperature of 950° C. or below;

rolling the steel at a starting temperature of 850° C. or above, and

cooling the steel after hot rolling at a starting temperature of 950° C. or less to a temperature of 700° C., at a rate of 20° C/sec or less.

2. The spring steel of claim 1 , which further has at least one element selected from a group consisting of Cu: 0.7% or less (exclusive of 0%) and Ni: 0.8% or less (exclusive of 0%).

3. The spring steel of claim 1 , which further has V: 0.4% or less (exclusive of 0%).

4. A steel wire obtained from the spring steel according to claim 1 .

5. A spring obtained from the spring steel according to claim 1 .

6. The spring steel of claim 1 , wherein the content of Si is in a range of from 1.97 to 2.5%.

7. The spring steel of claim 1 , having a content of Cu in a range of from 0.45 to 0.7 wt %.

8. A spring steel, having a composition consisting essentially of:

C: 0.47-0.65%,

Si: 1.7-2.5%,

Mn: 0.101%,

Cr: 0.051.9%,

P: >0.000%-0.015%,

S: 0.001%-0.015%,

Ti: 0.025-0.100%,

Al: 0.001%-0.05%,

N: 0.001-0.01%,

Nb: 0.02-0.05%;

optionally one or more of Cu, Ni, and V; and

a balance being Fe and inevitable impurities,

wherein said spring steel has a tensile strength of 2000 MPa or higher and a hydrogen embrittlement fatigue crack life of 712 sec. or higher, and said spring steel comprises a mass % of Ti nitride of:

[Ti with N ]≧3.42×[N]−0.354×[Al]−0.103×[Nb]  (1)

wherein said spring steel contains a mass % of Ti sulfide of:

[Ti with S ]≧1.49×[S]  (2)

wherein said spring steel contains a mass % Ti carbide of:

[Ti with C ]≧0.015  (3),

wherein [N], [Al], [Nb], and [S] represent an amount (mass %) of each element in the steel and the percentages above are mass percentages, and

wherein the spring steel is obtained by a process comprising:

cooling a steel having the composition within the range from 1,500° C. to 1,400° C. at a rate of 0.5° C./sec or less;

setting the heating temperature of the steel to at least 1,200° C. but no more that 1,300° C.;

spraying water on the hot steel before carrying out a hot-rolling process until the steel reaches a temperature of 950° C. or below;

rolling the steel at a starting temperature of 850° C. or above, and

cooling the steel after hot rolling at a starting temperature of 950° C. or less to a temperature of 700° C., at a rate of 20° C./sec or less.

9. The spring steel of claim 8 , which further has at least one element selected from a group consisting of Cu: 0.7% or less (exclusive of 0%) and Ni: 0.8% or less (exclusive of 0%).

10. The spring steel of claim 8 , which further has V: 0.4% or less.