Optimizing hydrogen generating efficiency in fuel cell cartridges
The present invention involves modifying certain characteristics of solid and aqueous chemical metal hydride fuels to increase the efficiency of hydrogen generation and/or to reduce the problems associated with such conventional hydride fuel sources. The present invention also relates to an apparatus ( 10 ) usable with the release of hydrogen from hydride-water fuel cells in which both the borohydride ( 110 ) and the water ( 210 ) components are in flowable or liquid form.
1. A method for increasing the efficiency of a metal hydride hydrogen-generating cartridge comprising the steps of:
forming a metal hydride slurry from a solid metal hydride and a liquid that is not reactive therewith in the absence of a stabilizing agent;
providing the metal hydride slurry in a separate compartment of the hydrogen-generating cartridge;
providing a predetermined amount of liquid reactant comprising predominantly water;
pressuring the metal hydride slurry, and
contacting the pressurized metal hydride slurry with the liquid reactant to create a reaction that generates hydrogen.
2. The method of claim 1 further comprising the step of grinding the solid metal borohydride, which has a first average particle size to a second average particle size that is smaller than the first average particle size before forming the metal hydride slurry.
3. The method of claim 2 , wherein the second average particle size is not more than about 25% of the first average particle size.
4. The method of claim 1 , wherein the metal hydride slurry is sufficiently flowable to enable liquid transport thereof.
5. The method of claim 1 , wherein the solid metal hydride is partially dissolved in the non-reactive liquid.
6. The method of claim 1 , wherein the metal hydride comprises sodium borohydride.
7. The method of claim 2 , wherein the step of increasing the surface area comprises grinding the second average particle size is about 0.5 mm or less.
8. The method of claim 7 , wherein the second average particle size is about 0.25 mm or less.
9. The method of claim 1 , wherein the liquid that is not reactive therewith in the absence of a stabilizing agent is an inorganic liquid.
10. The method of claim 1 , wherein the liquid reactant is pressurized before contacting the metal hydride slurry.
11. A method for producing hydrogen comprising the steps of:
dissolving a solid metal hydride fuel in a liquid comprising ammonia, hydrazine, tetraethyleneglycoldimethylether, or triethyleneglycoldimethylether, or a combination thereof, so as to form a liquid metal hydride fuel solution;
providing a predetermined amount of liquid reactant comprising predominantly water; and
combining the liquid reactant with the liquid metal hydride fuel solution to create a reaction that generates hydrogen.
12. The method of claim 11 , wherein the liquid metal hydride fuel solution is pressurized before combining with the liquid reactant.
13. The method of claim 11 , wherein the liquid reactant is pressurized before contacting the liquid metal hydride fuel solution.
14. The method of claim 11 , wherein the metal hydride fuel comprises a metal borohydride.
15. The method of claim 14 , wherein the metal borohydride comprises sodium borohydride.