Blend partner with natural rubber for elastomeric compounds
Natural rubber blends, methods for making the same, and articles made therefrom are provided. The natural rubber blend includes at least one propylene copolymer containing ethylene derived units. The natural rubber blend can further include one or more reinforcing fillers, such as carbon black. The presence of the propylene copolymer significantly improves the ozone resistance and ageing properties of the natural rubber gum stock.
1. A natural rubber blend, comprising:
100 phr natural rubber;
from about 5 to about 25 phr of one or more propylene-ethylene copolymers consisting of propylene and ethylene, said propylene-ethylene copolymers containing from about 10 to about 16 wt % ethylene and having a melting temperature (Tm) of from 60° C. to 105° C.; a heat of fusion of from about 40 J/g to about 80 J/g, and MFR ASTM-1238D, 2.16 kg, 230° C., of about from 1 g/10 min to about 90 g/10 min;
wherein (a) aging effect on tensile strength aged at 100° C., 72 h is at least one third less significant on said natural rubber blend than on a blend free of the propylene-ethylene copolymer, but is otherwise identical in terms of its constituents, and (b) aging effect on ultimate elongation aged at 70° C., 72 h is at least one half less significant on said natural rubber blend than on a blend free of the propylene-ethylene copolymer, but is otherwise identical in terms of its constituents.
2. The natural rubber blend of claim 1 , further comprising one or more reinforcing fillers.
3. The natural rubber blend of claim 2 , wherein the one or more reinforcing fillers is present in an amount of from about 50 phr to about 100 phr.
4. The natural rubber blend of claim 2 , wherein the one or more reinforcing fillers comprises carbon black.
5. The natural rubber blend of claim 1 , further comprising one or more thermoplastic resins.
6. The natural rubber blend of claim 5 , wherein the one or more thermoplastic resins comprises polypropylene.
7. A shaped article consisting essentially of the natural rubber blend of claim 1 .
8. A natural rubber blend, comprising:
100 phr natural rubber;
from about 5 to about 25 phr of one or more propylene-ethylene copolymers consisting of propylene and ethylene, said propylene-ethylene copolymers containing from about 10 to about 16 wt % ethylene, and having a melting temperature (Tm) of from 60° C. to 105° C.; a heat of fusion of from about 40 J/g to about 80 J/g; and MFR ASTM-1238D, 2.16 kg, 230° C., of from about 1 g/10 min to about 90 g/10 min;
5 phr of ZnO;
1 phr of stearic acid;
0.5 phr of (N-(1,3-dimethylbutyl)-N-phenyl-p-phenylenediamine);
0 to 5 phr of paraffinic oil;
2.5 phr of sulphur;
0.2 phr of diphenylguanidine; and
0.6 phr of dibenzothiazole disulphide,
wherein (a) aging effect on tensile strength aged at 100° C., 72 h is at least one third less significant on said natural rubber blend than on a blend free of the propylene-ethylene copolymer but is otherwise identical in terms of its constituents, and (b) aging effect on ultimate elongation aged at 70° C., 72 h is at least one half less significant on said natural rubber blend than on a blend free of the propylene-ethylene copolymer, but is otherwise identical in terms of its constituents.
9. A shaped article consisting essentially of the natural rubber blend of claim 8 .
10. A natural rubber blend, comprising:
100 phr natural rubber;
from about 5 to about 25 phr of one or more propylene-ethylene copolymers consisting of propylene and ethylene, said propylene-ethylene copolymers containing from about 10 to about 16 wt % ethylene, and having a melting temperature (Tm) of from 60° C. to 105° C., a heat of fusion of from about 40 J/g to about 80 J/g, and MFR ASTM-1238D, 2.16 kg, 230° C., of from about 1 g/10 min to about 90 g/10 min;
50 phr of one or more reinforcing fillers;
5 phr of ZnO;
2 phr of stearic acid;
1 phr of (N-(1,3-dimethylbutyl)-N-phenyl-p-phenylenediamine);
5 phr of aromatic oil;
2 phr of sulfur; and
1 phr of N-tertiarybutyl-2-benzothiazole sulfenamide.