Pellets comprising polymer and package containing the same
First pellets according to the present invention is characterized by satisfying all of the following requirements (Z), (1), (2), and (3): (Z) the pellet comprises a polymer (A) having an elastic modulus in tension of 100 MPa or less, (1) the pellets have an average weight per 30 pellets in the range of 0.80 to 2.00 g; (2) the pellets have a particle size distribution obtained by sieving in which pellets providing a maximum weight fraction account for 90 to 100% of the pellets; and (3) the pellets have a L ave /D ave value in the range of 1.00 to 1.70. Second pellets according to the present invention is characterized by satisfying the requirements of the (Z) and the following (4): (4) the pellets have a blocking force of 35 N or less that is measured after the pellets are left under a load at 35° C. for 24 hours and further at −10° C. for 7 days.
1. Pellets satisfying all of the following requirements (Z), (1), (2), (3) and (4):
(Z) the pellet comprises a polymer (A) having an elastic modulus in tension (an initial elastic modulus as measured by a method in accordance with ASTM D-638-03) of 100 MPa or less;
(1) the pellets have an average weight per 30 pellets in the range of 0.80 to 2.00 g;
(2) the pellets have a particle size distribution obtained by sieving in which pellets providing a maximum weight fraction account for 90 to 100% of the pellets;
(3) the pellets have a L ave /D ave value in the range of 1.00 to 1.5 wherein L ave and D ave are averages of the length L and the diameter D, respectively, of randomly selected 20 pellets and the length and the diameter are determined such that the length is larger than the diameter; and
(4) the pellets have a blocking force of 35 N or less as measured in a testing in which the blocking force is measured after the pellets are left under a load at 35° C. for 24 hours and further at −10° C. for 7 days.
2. The pellets according to claim 1 , wherein the polymer (A) is a polymer having a structural unit derived from an α-olefin.
3. The pellets according to claim 2 , wherein the polymer having a structural unit derived from an α-olefin is a copolymer having a structural unit derived from two or more kinds of α-olefins.
4. The pellets according to claim 3 , wherein the copolymer having a structural unit derived from two or more kinds of α-olefins is a copolymer (A-i) having a structural unit derived from ethylene and a structural unit derived from an α-olefin having 3 or more carbon atoms.
5. The pellets according to claim 3 , wherein the copolymer having a structural unit derived from two or more kinds of α-olefins is a copolymer (A-ii) having a structural unit derived from propylene and a structural unit derived from an α-olefin having 2 or more carbon atoms except for propylene.
6. The pellets according to any of claims 1 to 5 , wherein powders and/or liquid adheres on the surface of the pellets.
7. A package comprising a container packed with the pellets according to claims 1 to 5 in an amount of 15 to 1,500 kg.