Fluoropolymer composite composition
The present invention relates to a heat-meltable fluoropolymer composite composition having excellent thermal conductivity, gas and chemical liquid barrier properties and dynamic properties such as storage modulus which comprises a heat-meltable fluoropolymer fine powder and a layered-compound organized by treatment with tetraphenyl phosphonium ions. The present invention also relates to a heat-meltable fluoropolymer composite composition having similar properties to those mentioned above which is obtained by a process (I) in which a heat-meltable fluoropolymer composite composition is obtained by grinding and mixing a heat-meltable fluoropolymer fine powder and a layered-compound and a process (II) in which such heat-meltable fluoropolymer composite composition thus obtained is melted and mixed under shear stress by means of a melt-mixing extruder.
1. A process for manufacturing a heat-meltable fluoropolymer composite composition which comprises a step (I) in which a heat-meltable fluoropolymer composite composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound by use of a high-speed rotary mixer whose blades or cutter knives have a circumferential velocity of not less than 35 m/sec and a step (II) in which such heat-meltable fluoropolymer composite composition thus obtained is melt-mixed by exerting shear stress within a melt-mixing extruder.
2. The process for manufacturing a heat-meltable fluoropolymer composite composition according to claim 1 , wherein said heat-meltable fluoropolymer fine powder is an agglomerate powder having average particle size of not more than 10 μm which comprises agglomerated colloidal fine particles of heat-meltable fluoropolymer.
3. A heat-meltable fluoropolymer composite composition which is obtained by a step (I) in which a heat-meltable fluoropolymer composite composition is obtained by mixing a heat-meltable fluoropolymer fine powder and a layered-compound by use of a high-speed rotary mixer whose blades or cutter knives have a circumferential velocity of not less than 35 m/sec and a step (II) in which such heat-meltable fluoropolymer composite composition thus obtained is melt-mixed by exerting shear stress within a melt-mixing extruder.
4. The heat-meltable fluoropolymer composite composition according to claim 3 , wherein said layered-compound is organically modified with onium ions.
5. The heat-meltable fluoropolymer composite composition according to claim 3 , wherein said layered-compound is at least one selected from the group consisting of clay mineral, mica and graphite which is not more than 10 μm in average particle size.
6. The heat-meltable fluoropolymer composite composition according to claim 3 , whose nitrogen gas transmission rate is not more than 0.60 times as high as that of heat-meltable fluoropolymer containing no layered-compound.
7. The heat-meltable fluoropolymer composite composition according to claim 3 , whose storage modulus at 25° C. is not less than 1.5 times as high as that of heat-meltable fluoropolymer containing no layered-compound.
8. The heat-meltable fluoropolymer composite composition according to claim 3 , whose specific thermal conductivity is not less than 2 times as high as that of heat-meltable fluoropolymer containing no layered-compound.