Polyolefin elastomer composition for artificial leather applications

1. A process for the production of a supported artificial leather comprising the steps of:

(a) forming a thermoplastic polyolefin composition into a powder, said composition comprising:

(i) an olefin block copolymer, having:

(i)(1) a Shore A hardness greater than 75,

(i)(2) a Tg less than −45° C.,

and

(i)(3) a distinct melting peak greater than 95° C. as determined by DSC

or

(ii) a blend of:

(ii)(1) a linear ethylene polymer, a substantially linear ethylene polymer, or mixtures thereof characterized as having:

(ii)(1)(a) a density of less than about 0.93 g/cm 3 ,

(ii)(1)(b) a molecular weight distribution, M w /M n , of less than about 3.0,

and

(ii)(1)(c) a Composition Distribution Branch Index of greater than 30 percent,

and

(ii)(2) a propylene polymer having a crystallinity equal to or greater than 30 percent

(b) coating a release paper with said powder,

(c) heating said coating to form a continuous polymeric layer,

(d) applying a fabric to heated continuous polymeric layer forming a fabric/polymeric layer composite,

(e) applying pressure to the heated fabric/polymeric layer composite,

(f) cooling said fabric/polymeric composite layer, and

(g) stripping the release paper from the continuous polymeric layer forming an artificial leather.

2. A process for the production of an unsupported artificial leather comprising the steps of:

(a) forming a thermoplastic polyolefin composition into a powder, said composition comprising:

(i) an olefin block copolymer, having:

(i)(1) a Shore A hardness greater than 75,

(i)(2) a Tg less than −45° C.,

and

(i)(3) a distinct melting peak greater than 95° C. as determined by DSC

or

(ii) a blend of:

(ii)(1) a linear ethylene polymer, a substantially linear ethylene polymer, or mixtures thereof characterized as having:

(ii)(1)(a) a density of less than about 0.93 g/cm 3 ,

(ii)(1)(b) a molecular weight distribution, M w /M n , of less than about 3.0,

and

(ii)(1)(c) a Composition Distribution Branch Index of greater than 30 percent,

and

(ii)(2) a propylene polymer having a crystallinity equal to or greater than 30 percent

(b) coating a release paper with said powder,

(c) heating said coating to form a continuous polymeric layer,

(f) cooling said polymeric layer,

and

(g) stripping the release paper from the continuous polymeric layer forming an artificial leather.

3. The process of claims 1 or 2 wherein the

(i) olefin block copolymer is further characterized by one or more of the aspects described as follows:

(i.a) has a weight average molecular weight/number average molecular weight ratio (Mw/Mn) from about 1.7 to about 3.5, at least one melting peak (Tm) in degrees Celsius, and a density (d) in grams/cubic centimeter (g/cc), wherein the numerical values of Tm and d correspond to the relationship:

T m >−2002.9+4538.5( d )−2422.2( d ) 2 or T m >−6553.3+13735( d )−7051.7( d ) 2 ; or

(i.b) has a Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion (ΔH) J/g and a delta quantity, ΔT, in degrees Celsius defined as the temperature difference between the tallest differential scanning calorimetry (DSC) peak and the tallest crystallization analysis fractionation (CRYSTAF) peak, wherein the numerical values of ΔT and ΔH have the following relationships:

Δ T>− 0.1299(Δ H )+62.81 for Δ H greater than zero and up to 130 J/g,

Δ T≧ 48° C. for Δ H greater than 130 J/g,

wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30° C.; or

(i.c) is characterized by an elastic recovery (Re) in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/alpha-olefin interpolymer, and has a density (d) in grams/cubic centimeter (g/cc), wherein the numerical values of Re and d satisfy the following relationship when ethylene/alpha-olefin interpolymer is substantially free of a cross-linked phase: Re>1481-1629(d); or

(i.d) has a molecular fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content greater than, or equal to, the quantity (−0.2013) T+20.07, more preferably greater than or equal to the quantity (−0.2013) T+21.07, where T is the numerical value of the peak elution temperature of the TREF fraction, measured in ° C.; or

(i.e) has a storage modulus at 25° C. (G′(25° C.)) and a storage modulus at 100° C. (G′(100° C.)) wherein the ratio of G′(25° C.) to G′(100° C.) is in the range of about 1:1 to about 9:1 or

(i.f) has a molecular fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3; or

(i.g) has an average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn, greater than about 1.3.

4. The process of claim 1 or 2 wherein the thermoplastic polyolefin composition is formed into a powder by pulverizing said thermoplastic polyolefin composition at ambient temperature.

5. The process of claim 2 wherein the unsupported artificial leather is used as a skin for an instrument panel, a console box, an arm rest, a head rest, a door trim, a rear panel, a pillar trim, a sunvisor, a trunk room trim, a trunk lid trim, an air bag cover, a seat buckle, a head liner, a gloves box, or a steering wheel cover.

6. The process of claim 1 wherein the supported artificial leather is used as a skin for an instrument panel, a console box, an arm rest, a head rest, a door trim, a rear panel, a pillar trim, a sunvisor, a trunk room trim, a trunk lid trim, an air bag cover, a seat buckle, a head liner, a gloves box, or a steering wheel cover.