Water retention agent for cementitious compositions and cementitious compositions containing same
A water retention agent for a cementitious composition, characterized in that it takes the form of a liquid aqueous suspension of at least one polysaccharide at a mass concentration of between 15 and 30% in an aqueous solution of a strong base salt, excluding ammonium salts, with an anionic strength of between 1.25 mol/L and 15 mol/L, having a pH greater than 9 and containing an attapulgite in micronized form and at least one non-phyllitic mineral powder, referred to hereafter as filler, which is chemically inert in the aqueous suspension and which has a grain size of between 0.1 and 100 micrometers, the aqueous suspension being stable at least in a temperature range of between 5° C. and 30° C. The water retention agent is suitable for increasing both the viscosity and the water retention capacity of cementitious compositions without affecting the spreading ability thereof.
1. A water retention agent for a cementitious composition, comprising a liquid aqueous suspension of:
at least one polysaccharide at a concentration by weight of between 15% and 30%,
in an aqueous solution of a strong base salt, with the exception of ammonium salts, having an ionic strength of between 1.25 mol/l and 15 mol/l, and a pH of greater than 9,
micronized attapulgite, and
filler comprising at least one nonphyllitic mineral powder, the content by weight of said filler being between 0.1% and 5% of said aqueous suspension,
wherein the micronized attapulgite and filler are chemically inert in said aqueous suspension, have a particle size of between 0.1 and 100 micrometers, and confer stability on said aqueous suspension within a temperature range of at least 5° C. to 30° C.
2. The water retention agent as claimed in claim 1 , wherein the content by weight of attapulgite in the aqueous suspension is between 0.1% and 5%.
3. The water retention agent as claimed in claim 1 , wherein the aqueous solution exhibits an ionic strength of between 2.5 mol/l and 12.5 mol/l.
4. The water retention agent as claimed in claim 1 , wherein the filler is a siliceous filler, with a density of between 2.60 and 2.80 g/ml.
5. The water retention agent as claimed in claim 1 , wherein the filler exhibits a particle size curve having a D50 value between 1 μm and 12 μm.
6. The water retention agent as claimed in claim 1 , wherein the concentration by weight of the polysaccharide(s) is between 18% and 25% of said aqueous suspension.
7. The water retention agent as claimed in claim 1 , wherein the at least one polysaccharide exhibits, dry, a particle size curve having a D50 value between 10 μm and 200 μm.
8. The water retention agent as claimed in claim 1 , wherein the at least one polysaccharide is a hydroxyalkylcellulose or a hydroxyalkyl guar comprising a C 2 to C 8 alkyl group, or a mixture thereof.
9. The water retention agent as claimed in claim 8 , wherein the hydroxyalkylcellulose is a hydroxyethylcellulose (HEC), a methylhydroxypropylcellulose (MHPC), a hydrophobic modified hydroxyethylcellulose (HMHEC), or a mixture thereof.
10. A process for increasing the viscosity of a cementitious composition and its ability to retain water, comprising adding the water retention agent as claimed in claim 1 to the cementitious composition.
11. The process as claimed in claim 10 , wherein the addition of the water retention agent does not affect the spreading of the cementitious composition.
12. A cementitious composition based on cement and water, comprising the water retention agent as claimed in claim 1 in an amount of between 0.1% and 5% by weight of the cement.
13. The water retention agent as claimed in claim 1 , wherein the content by weight of attapulgite in the aqueous suspension is between 0.2% and 0.8%.
14. The water retention agent as claimed in claim 4 , wherein the filler is a crystalline siliceous filler.
15. The water retention agent as claimed in claim 1 , wherein the filler exhibits a particle size curve having a D50 value between 2 μm and 8 μm.
16. The water retention agent as claimed in claim 1 , wherein the content by weight of filler is between 0.35% and 1.5% of said aqueous suspension.
17. The water retention agent as claimed in claim 1 , wherein the at least one polysaccharide exhibits, dry, a particle size curve having a D50 value between 50 μm and 150 μm.