Compositions and methods for well completions
Expansive cements for use in cementing subterranean wells contain an encapsulated gas-generating substance. The gas-generating substance comprises one or more materials that release hydrogen, nitrogen or both. The gas-generating substance is encapsulated by a coating comprising a polymer. The coating prevents premature gas release at the surface during slurry mixing, and promotes gas release at a desired location in the subterranean well. The released gas may also control the internal pore pressure of the cement slurry, thereby inhibiting the invasion of formation fluids into the borehole.
1. A method for cementing a subterranean well, comprising:
(i) preparing a well-cementing composition comprising water, an inorganic cement and an additive comprising particles comprising a gas-generating substance that is encapsulated by coating comprising a polymer, wherein the gas-generating substance comprises one or more materials that release hydrogen, nitrogen or both; and
(ii) placing the composition in the well,
wherein the additive particle size is between about 2 μm and 2000 μm.
2. The method of claim 1 , wherein the gas-generating materials that release hydrogen comprise one or more members of the list comprising aluminum, calcium, zinc, iron, magnesium, lithium, sodium and potassium.
3. The method of claim 1 , wherein the gas-generating materials that release nitrogen comprise one or more members of the list comprising azodicarbonamide, sodium azodicarboxylate, azobismethyl propionitrite and p-toluenesulfonhydrazide.
4. The method of claim 1 , wherein the coating comprises one or more members selected from the group consisting of styrene-butadiene copolymer latexes, acrylic resins, styrene/acrylic copolymer resins, acrylic ester resins, methylcellulose, ethylcellulose, hydroxypropylcellulose, and polyvinylidene chloride.
5. The method of claim 4 , wherein the molecular weight of the styrene-butadiene copolymer is between about 1.5·10 5 g/mol and about 4.0·10 5 g/mol.
6. The method of claim 1 , wherein the coating is present at a concentration up to about 20% by weight of gas-generating material.
7. A method for controlling the liberation of gas from a gas-generating agent, comprising:
(i) providing particles comprising a gas-generating substance, wherein the gas-generating substance comprises one or more materials that release hydrogen, nitrogen or both; and
(ii) coating the particle surfaces with a material comprising a polymer, thereby encapsulating the particles,
wherein the additive particle size is between about 2 μm and 2000 μm.
8. The method of claim 7 , wherein the gas-generating material releases hydrogen, and comprises one or more members of the list comprising aluminum, calcium, zinc, iron, magnesium, lithium, sodium and potassium.
9. The method of claim 7 , wherein the gas-generating material releases nitrogen, and comprises one or more members of the list comprising azodicarbonamide, sodium azodicarboxylate, azobismethyl propionitrite and p-toluenesulfonhydrazide.
10. The method of claim 7 , wherein the coating comprises one or more members selected from the group consisting of styrene-butadiene copolymer latexes, acrylic resins, styrene/acrylic copolymer resins, acrylic ester resins, methylcellulose, ethylcellulose, hydroxypropylcellulose, and polyvinylidene chloride.
11. The method of claim 10 , wherein the molecular weight of the styrene-butadiene copolymer is between about 1.5·10 5 g/mol and about 4.0·10 5 g/mol.
12. The method of claim 7 , wherein the coating is present at a concentration up to about 20% by weight of gas-generating material.
13. A method for controlling the internal pore pressure of a well-cementing composition in a subterranean well, comprising:
(i) preparing a well-cementing composition comprising water, an inorganic cement and an additive comprising particles comprising a gas-generating substance that is encapsulated by a coating comprising a polymer, wherein the gas-generating substance comprises one or more materials that release hydrogen, nitrogen or both;
(ii) placing the composition in the well; and
(iii) allowing the coating to degrade, thereby exposing the gas-generating material to water, thereby causing the liberation of gas, thereby pressurizing the well-cementing composition,
wherein the additive particle size is between about 2 μm and 2000 μm.
14. The method of claim 13 , wherein the gas-generating material releases hydrogen, and comprises one or more members of the list comprising aluminum, calcium, zinc, iron, magnesium, lithium, sodium and potassium.
15. The method of claim 13 , wherein the gas-generating material releases nitrogen, and comprises one or more members of the list comprising azodicarbonamide, sodium azodicarboxylate, azobismethyl propionitrite and p-toluenesulfonhydrazide.
16. The method of claim 13 , wherein the coating comprises one or more members selected from the group consisting of styrene-butadiene copolymer latexes, acrylic resins, styrene/acrylic copolymer resins, acrylic ester resins, methylcellulose, ethylcellulose, hydroxypropylcellulose, and polyvinylidene chloride.
17. The method of claim 13 , wherein the coating is present at a concentration up to about 20% by weight of gas-generating material.