Method for cutting C—Mn steel with a fiber laser
The invention relates to a laser cutting method for cutting a C—Mn steel workpiece, characterized in that laser beam generation means comprising at least one silica fiber with an ytterbium-doped core is used to generate the laser beam. Preferably, the ytterbium-based fiber has a wavelength between 1.07 and 1.1 μm, preferably 1.07 μm, the quality factor of the laser beam is between 0.33 and 8 mm.mrad, and the laser beam has a power of between 0.1 and 25 kW. The assistance gas for the laser beam is chosen from nitrogen, helium, argon, oxygen, CO 2 and mixtures thereof, and, optionally, it further contains one or more additional compounds chosen from H 2 and CH 4 .
1. A laser cutting method for cutting a C—Mn steel workpiece, wherein laser beam generation means comprising at least one ytterbium-containing fiber for generating a laser beam and an assistance gas for the laser beam are used, and in that the workpiece to be cut has a thickness between 2 mm and 30 mm, the quality factor of the laser beam is between 1 mm.mrad and 8 mm.mrad, and the assistance gas for said laser beam is oxygen and the assistance gas pressure is between 0.2 bar and 0.1 bar.
2. The method of claim 1 , wherein said fiber is formed from an ytterbium-doped core clad with silica.
3. The method of claim 1 , wherein said laser beam generated by the ytterbium-based fiber has a wavelength between 1 and 5 μm.
4. The method of claim 1 , wherein said laser beam generated by the ytterbium-based fiber has a wavelength between 1.07 and 1.1 μm.
5. The method of claim 1 , wherein said laser beam has a power of between 0.1 kW and 25 kW.
6. The method of claim 1 , wherein said laser beam is a continuous or pulsed laser beam.
7. The method of claim 1 , wherein the workpiece to be cut has a thickness between 2 mm and 20 mm.
8. The method of claim 1 , wherein said cutting speed is between 0.1 mm and 20 m/min.
9. The method of claim 1 , wherein the quality factor of said laser beam is greater than 2 mm.mrad and less than 7 mm.mrad.