Power storage device
An object is to increase the amount of ions capable of entering and leaving a positive electrode active material in an ion battery so that the capacity of the battery is increased. When a solid solution including alkali metal oxide having electrical conductivity less than or equal to 10 −10 S/cm and including alkali metal with a valence of 2 or more, and alkali metal oxide having electrical conductivity greater than or equal to 1×10 −6 S/cm and less than or equal to 3×10 −6 S/cm is used as a positive electrode active material in an ion battery, the amount of ions capable of entering and leaving the positive electrode active material is increased, so that the capacity of the battery is increased.
1. A power storage device comprising:
a positive electrode comprising a solid solution,
wherein the solid solution comprises a first alkali metal oxide and a second alkali metal oxide,
wherein the solid solution has an electrical conductivity greater than or equal to 1 × 10 −7 S/cm and less than or equal to 10 ×10 −7 S/cm,
wherein the first alkali metal oxide is Li 2 MnO 3 ,
wherein the second alkali metal oxide is LiCo 1/3 Mn 1/3 Ni 1/3 O 2 , and
wherein the positive electrode is formed by a sputtering method by using a target comprising the solid solution.
2. The power storage device according to claim 1 ,
wherein the solid solution has a layered structure, and
wherein the solid solution is Li 2 MnO 3 —LiCo 1/3 Mn 1/3 Ni 1/3 O 2 .
3. A power storage device comprising:
a positive electrode comprising a solid solution,
wherein the solid solution comprises a first alkali metal oxide and a second alkali metal oxide,
wherein the solid solution has an electrical conductivity greater than or equal to 1 ×10 −7 S/cm and less than or equal to 10 ×10 −7 S/cm,
wherein the first alkali metal oxide is any of Li 2 MnSiO 4 and Li 2 FeSiO 4 ,
wherein the second alkali metal oxide is any of LiCoO 2 , LiMn 2 O 4 , and LiNiO 2 , and
wherein the positive electrode is formed by a sputtering method by using a target comprising the solid solution.
4. A power storage device comprising:
a first conductive wiring electrically connected to a battery cover;
a second conductive wiring electrically connected to a battery bottom which is insulated from the battery cover; and
an electrode body provided with an upper insulating plate and a lower insulating plate,
wherein the electrode body comprises:
a positive electrode comprising a solid solution, and electrically connected to the first conductive wiring through the upper insulating plate;
a negative electrode electrically connected to the second conductive wiring through the lower insulating plate; and
a separator provided between the positive electrode and the negative electrode,
wherein the solid solution comprises a first alkali metal oxide and a second alkali metal oxide,
wherein the solid solution has an electrical conductivity greater than or equal to 1 ×10 −7 S/cm and less than or equal to 10 −10 −7 S/cm,
wherein the first alkali metal oxide is any of Li 2 MnSiO 4 and Li 2 FeSiO 4 ,
wherein the second alkali metal oxide is any of LiCoO 2 , LiMn 2 O 4 , and LiNiO 2 , and
wherein the positive electrode is formed by a sputtering method by using a target comprising the solid solution.
5. The power storage device according to claim 1 , wherein the positive electrode further comprises a conductive agent and a binder.
6. The power storage device according to claim 5 , wherein the conductive agent is a graphite of a carbon fiber.
7. The power storage device according to claim 3 , wherein the positive electrode further comprises a conductive agent and a binder.
8. The power storage device according to claim 7 , wherein the conductive agent is a graphite of a carbon fiber.
9. The power storage device according to claim 4 , wherein the positive electrode further comprises a conductive agent and a binder.
10. The power storage device according to claim 9 , wherein the conductive agent is a graphite of a carbon fiber.
11. A sputtering target comprising a solid solution and a conductive agent,
wherein the solid solution is Li 2 MnO 3 —LiCo 1/3 Mn 1/3 Ni 1/3 O 2 , and
wherein the solid solution has an electrical conductivity greater than or equal to 1 ×10 −7 S/cm and less than or equal to 10 ×10 −7 S/cm.
12. The sputtering target according to claim 11 , wherein the conductive agent is a graphite of a carbon fiber.