Optical member, plastic lens for eyeglasses, and method for manufacturing the same
An optical member includes a substoichiometric titanium oxide film formed by depositing substoichiometric titanium oxides in a vacuum chamber into which an oxygen gas for adjusting a vacuum is introduced. In the optical member, the film forming pressure p (Pa) in the vacuum chamber and the optical film thickness (a refractive index of 2.50, a wavelength of 500 nm) of the substoichiometric titanium oxide film have relations of (1) p≧0.005, (2) optical film thickness ≦0.500λ, and (3) optical film thickness ≧(0.001exp(905.73p)−0.050)λ where exp is an exponential function with e as the base of the natural logarithm.
1. An optical member, comprising
a substoichiometric titanium oxide film formed by depositing a substoichiometric titanium oxide in a vacuum chamber into which an oxygen gas for adjusting a vacuum is introduced, wherein
a film forming pressure p (Pa) in the vacuum chamber and an optical film thickness (a refractive index of 2.50, a wavelength of 500 nm) of the substoichiometric titanium oxide film have relations:
0.0067 ≧p≧ 0.005, (1)
optical film thickness≦0.450λ, and (2)
optical film thickness≧(0.001exp(905.73 p )−0.050)λ (3)
where exp is an exponential function with e as a base of natural logarithm.
2. The optical member according to claim 1 , wherein
a relation (3-1) is employed in place of the relation (3):
optical film thickness≧(0.001exp(905.73 p ))λ (3-1)
where exp is an exponential function with e as a base of natural logarithm.
3. The optical member according to claim 1 , wherein the substoichiometric titanium oxide film is formed by depositing while being assisted by at least an oxygen ion or an argon ion or while being treated with plasma.
4. The optical member according to claim 1 , wherein the substoichiometric titanium oxide film is a high refractive index layer in an anti-reflective coating containing a low refractive index layer and the high refractive index layer.
5. A plastic lens for eyeglasses, wherein the optical member as claimed in claim 1 is used.
6. The plastic lens for eyeglasses according to claim 5 , further comprising a hard coat layer.
7. A method for manufacturing an optical member, comprising
depositing a substoichiometric titanium oxide in a vacuum chamber into which an oxygen gas for adjusting a vacuum is introduced to form a substoichiometric titanium oxide film on a substrate, wherein
a film forming pressure p (Pa) in the vacuum chamber and an optical film thickness (a refractive index of 2.50, a wavelength of 500 nm) of the substoichiometric titanium oxide film have relations:
0.0067≧ p≧ 0.005, (1)
optical film thickness≦0.450λ, and (2)
optical film thickness≧(0.001exp(905.73 p )−0.050)λ (3)
where exp is an exponential function with e as a base of natural logarithm.
8. The method for manufacturing an optical member according to claim 7 , wherein a relation (3-1) is employed in place of the relation (3):
optical film thickness≧(0.001exp(905.73 p ))λ (3-1)
where exp is an exponential function with e as a base of natural logarithm.
9. The method for manufacturing an optical member according to claim 7 , wherein
the deposition is carried out while being assisted by an oxygen ion and/or an argon ion or while being treated with plasma.
10. The method for manufacturing an optical member according to claim 7 , wherein
the substoichiometric titanium oxide film is formed as a high refractive index layer in an anti-reflective coating containing a low refractive index layer and the high refractive index layer.
11. A method for manufacturing a plastic lens for eyeglasses, comprising
manufacturing a plastic lens for eyeglasses by using the manufacturing method as claimed in claim 7 .
12. The method for manufacturing a plastic lens for eyeglasses according to claim 11 , wherein
a hard coat layer is formed prior to the formation of the substoichiometric titanium oxide film.