Abrasion and corrosion resistant alloy and hardfacing/cladding applications
Weld deposit compositions with improved abrasion and corrosion resistance are provided by balancing percent weights of Chromium (Cr), Titanium (Ti), Niobium (Nb), and Boron (B) to allow the Chromium content of the weld matrix to be minimally reduced during carbide formation. The result is an enriched Chromium matrix that has excellent corrosion resistance in combination with highly abrasion resistant dispersed carbides.
1. A weld deposit composition for a GMAW application comprising, by percent mass:
between approximately 1.8% and approximately 2.5% Carbon;
between approximately 0.8% and approximately 1.4% Manganese;
between approximately 0.6% and approximately 1.2% Silicon;
between approximately 23.0% and approximately 26.0% Chromium;
between approximately 2.0% and approximately 3.0% Nickel;
between approximately 0.7% and approximately 1.5% Molybdenum;
between approximately 2.6% and approximately 3.6% Niobium;
less than approximately 0.5% Titanium;
between approximately 0.3% and approximately 0.8% Boron;
between approximately 0% and approximately 0.4% Zirconium; and
a balance comprising Iron;
wherein the amount of Niobium and Titanium are balanced with the amount of Boron to form intermetallic borides therewith.
2. The weld deposit composition according to claim 1 , wherein the Carbon comprises approximately 2.2%.
3. The weld deposit composition according to claim 1 , wherein the Manganese comprises approximately 1.1%.
4. The weld deposit composition according to claim 1 , wherein the Silicon comprises approximately 0.8%.
5. The weld deposit composition according to claim 1 , wherein the Chromium comprises approximately 24.5%.
6. The weld deposit composition according to claim 1 , wherein the Nickel comprises approximately 2.5%.
7. The weld deposit composition according to claim 1 , wherein the Molybdenum comprises approximately 1.1%.
8. The weld deposit composition according to claim 1 , wherein the Niobium comprises approximately 3.0%.
9. The weld deposit composition according to claim 1 , wherein the Titanium comprises approximately 0.2%.
10. The weld deposit composition according to claim 1 , wherein the Boron comprises approximately 0.6%.
11. The weld deposit composition according to claim 1 , wherein the Zirconium comprises approximately 0%.
12. A welding wire capable of producing a weld deposit according to claim 1 .
13. A welded structure comprising a weld deposit according to claim 1 .
14. The welded structure according to claim 13 , wherein the welded structure is selected from the group consisting of pipes, plates, and vessels.
15. A weld deposit composition for an FCAW application comprising, by percent mass:
between approximately 3.7% and approximately 4.3% Carbon;
between approximately 0.8% and approximately 1.2% Manganese;
between approximately 0.3% and approximately 1.0% Silicon;
between approximately 24.0% and approximately 26.0% Chromium;
between approximately 1.3% and approximately 2.0% Molybdenum;
between approximately 2.6% and approximately 3.6% Niobium;
less than approximately 0.3% Titanium;
between approximately 0.4% and approximately 0.9% Boron;
between approximately 0.1% and approximately 0.4% Zirconium; and
a balance comprising Iron;
wherein the amount of Niobium and Titanium are balanced with the amount of Boron to form intermetallic borides therewith.
16. The weld deposit composition according to claim 15 , wherein the Carbon comprises approximately 4.0%.
17. The weld deposit composition according to claim 15 , wherein the Manganese comprises approximately 1.0%.
18. The weld deposit composition according to claim 15 , wherein the Silicon comprises approximately 0.5%.
19. The weld deposit composition according to claim 15 , wherein the Chromium comprises approximately 25.0%.
20. The weld deposit composition according to claim 15 , wherein the Molybdenum comprises approximately 1.5%.
21. The weld deposit composition according to claim 15 , wherein the Niobium comprises approximately 3.0%.
22. The weld deposit composition according to claim 15 , wherein the Titanium comprises approximately 0.1%.
23. The weld deposit composition according to claim 15 , wherein the Boron comprises approximately 0.75%.
24. The weld deposit composition according to claim 15 , wherein the Zirconium comprises approximately 0.25%.
25. A welding wire capable of producing a weld deposit according to claim 15 .
26. A welded structure comprising a weld deposit according to claim 15 .
27. The welded structure according to claim 26 , wherein the welded structure is selected from the group consisting of pipes, plates, and vessels.