Anti-glare glass sheet having compressive stress equipoise and methods thereof
A chemically-strengthened glass sheet including: a smooth first side; and a rough second side, wherein the compressive stress values of the smooth first-side and the rough second-side are substantially in equipoise. Methods of making and using the glass sheet, as defined herein, are disclosed. A display system that incorporates the glass sheet, as defined herein, is also disclosed.
1. A chemically-strengthened glass sheet comprising:
a smooth first side; and
a rough second side,
wherein the compressive stress values of the smooth first side and the rough second side are substantially in equipoise, and the smooth first side has an RMS roughness less than about 10 nm and the rough second side has an RMS roughness greater than about 50 nm.
2. The glass sheet of claim 1 wherein the difference between the compressive stress values of the smooth first side and the rough second side is less than about 2%.
3. The glass sheet of claim 1 wherein the compressive stress value of the smooth first side is greater than about 400 MPa, the compressive stress value of the rough second side is greater than about 400 MPa, and the difference in the compressive stress values between the two sides of the glass sheet is less than about 10 MPa.
4. The glass sheet of claim 1 , wherein the chemically strengthened glass article contains greater than about 2 mol % Al 2 O 3 , ZrO 2 , or both.
5. The glass sheet of claim 1 , wherein the chemically strengthened glass article has a surface compressive stress greater than about 350 MPa and an ion-exchange depth-of-layer greater than 15 microns.
6. The glass sheet of claim 1 , wherein the chemically strengthened glass article contains less than about 4 mol % CaO.
7. The glass sheet of claim 1 wherein the sheet has anti-glare properties comprising a 20 degree reflective DOI of less than 90 and transmission haze of less than 50.
8. The glass sheet of claim 1 where the sheet is at least 200 mm×200 mm in size and the maximum waviness of the sheet after chemical strengthening is less than 200 microns.