Transition metal phosphate, production process thereof, positive electrode, and sodium secondary battery
The present invention provides a transition metal phosphate and a production process thereof, a positive electrode, and a sodium secondary battery. The transition metal phosphate contains sodium (Na), phosphorus (P) and a transition metal element and having a BET specific surface area of 1 m 2 /g to 50 m 2 /g. The process for producing a transition metal phosphate comprises steps (1) and (2): (1) a step of bringing a phosphorus (P) source, a sodium (Na) source, an M source (M is one or more transition metal elements) and water into contact with each other, and obtaining a liquid material thereby, and (2) a step of separating water from the liquid material and obtaining a transition metal phosphate thereby.
1. A transition metal phosphate, containing sodium (Na), phosphorus (P) and a transition metal element; having a BET specific surface area of 3 m 2 /g to 50 m 2 /g; and being represented by the following formula (I):
Na x M y PO 4 (I)
wherein
x is from more than 0 and not more than 1.5,
y is from 0.8 to 1.2, and
M is one or more transition metal elements.
2. The transition metal phosphate according to claim 1 , having an orthorhombic crystal structure.
3. The transition metal phosphate according to claim 1 wherein M contains Fe or Mn.
4. The transition metal phosphate according to claim 1 , wherein the transition metal phosphate is composed of particles, and D50 of the particles is from 0.01 to 50 μm (D50 indicates the value of particle diameter at which the cumulative volume calculated from the smallest particle diameter side reaches 50% in the volume-based cumulative particle size distribution).
5. A positive electrode active material for sodium secondary batteries, the material comprising the transition metal phosphate according to claim 1 .
6. A positive electrode for sodium secondary batteries, the electrode comprising the positive electrode active material according to claim 5 .
7. A sodium secondary battery, comprising the positive electrode according to claim 6 .
8. The sodium secondary battery according to claim 7 , which further comprises a separator.
9. The sodium secondary battery according to claim 8 , wherein the separator comprises a porous laminate film in which a heat-resistant porous layer containing a heat-resistant resin and a porous film containing a thermoplastic resin are stacked each other.
10. A process for producing the transition metal phosphate of claim 1 , the process comprising the following steps (1) and (2):
(1) a step of bringing a phosphorus (P) source, a sodium (Na) source, an M source (M is one or more transition metal elements) and water into contact with each other, and obtaining a liquid material thereby, and
(2) a step of separating water from the liquid material and obtaining a transition metal phosphate thereby.
11. The production process according to claim 10 , wherein, in the step (1), an aqueous solution containing P and Na is brought into contact with an M compound or an aqueous solution containing an M compound and obtain the liquid material thereby.
12. The production process according to claim 10 , wherein, in the step (1), an aqueous solution containing Na and M is brought into contact with an aqueous solution containing P and obtain the liquid material thereby.
13. The production process according to claim 10 , wherein M contains a divalent transition metal element.
14. The production process according to claim 10 , wherein M contains Fe or Mn.
15. The production process according to claim 10 , wherein the step (2) comprises a step of evaporating water.
16. The production process according to claim 15 , wherein the evaporation is performed by heating.