Use of temperature and ethylene partial pressure to introduce long chain branching in high density polyethylene
The invention describes the preparation of long chain branching in high density polyethylene by using metallocene catalysts in the presence of ethylene.
1. A long chain branched high density ethylene polymer having:
at least 95 mol % ethylene;
a density of from 0.950 g/cm 3 to 0.96 g/cm 3 ;
an Mw/Mn of 4.5 or less;
a melt index (190° C., 2.16 kg) of 5 dg/min or less;
an Mw within a range of from 68,945 to 133,530;
a g′ (Zave) within a range of from 0.89 to 0.925;
high load melt index (190° C., 21.6 kg) within a range of from 2.16 to 108.35 dg/min;
a melt index ratio (MIR) within a range of from 31.43 to 64.73; and
wherein polyethylene having an Mw of 1000 or less are present at less than 5 wt %, based upon the weight of the polyethylene polymer;
and produced by a method of combining ethylene and a bridged or unbridged bis-indenyl or bis-tetrahydroindenyl metallocene catalyst compound.
2. The ethylene polymer of claim 1 , wherein polyethylene having an Mw of 1000 g/mol or less are not detected by DRI GPC.
3. The ethylene polymer of claim 1 , wherein both g′ (Z ave) and MIR increase with molecular weight distribution.
4. The ethylene polymer of claim 1 , wherein the polymer has less than 0.08 vinyl groups per 1000 carbons.
5. The ethylene polymer of claim 1 , wherein the polymer has less than 0.4 vinylene groups per 1000 carbons.
6. The ethylene polymer of claim 1 , wherein the polymer has an Mw/Mn below 4.0.
7. The ethylene polymer of claim 1 , wherein the polymer has a gel stiffness of more than 10,000 Pa*s n .
8. The ethylene polymer of claim 1 , wherein the polymer has a relaxation exponent, n, between 0.35 and 0.85.
9. The ethylene polymer of claim 1 , wherein the polymer has a gel stiffness of more than 10,000 Pa*s n and a relaxation exponent, n, between 0.35 and 0.85.
10. The ethylene polymer of claim 1 , wherein the polymer has a Tm (° C.) of 125° C. or more.
11. The ethylene polymer of claim 1 , wherein the polymer has a Tm (° C.) of 130° C. or more.
12. The ethylene polymer of claim 1 , wherein the polymer has an Mz of 150,000 g/mol or more.
13. The ethylene polymer of claim 1 , wherein the polymer has 3 mol % or less of comonomer.
14. The ethylene polymer of claim 1 , wherein the catalyst compound is a bridged bis-tetrahydroindenyl zirconocene catalyst compound.