Lithium ion secondary battery
A positive electrode capable of achieving both of high volumetric energy density and high volumetric power density and a lithium ion secondary battery using the same are provided. A lithium ion secondary battery includes a positive electrode including a current collector with a positive active material mixture layer applied on both faces thereof, the positive active material mixture layer including active material particles, conductive additive particles and a binder. The active material particles used have a value D of an average particle diameter D50 of the active material particles in the range from 1 to 10 μm. The ratio b/a of the volume fraction b of the vacancy volume in the positive active material mixture layer to the volume fraction a of the active material particles in the positive active material mixture layer is in the range of −0.01D+0.57≦b/a≦−0.01D+0.97.
1. A lithium ion secondary battery, comprising a positive electrode including a current collector with a positive active material mixture layer applied thereon, the positive active material mixture layer including:
active material particles;
conductive additive particles comprising a carbonaceous material; and
a binder,
wherein the ranges of 1 μm≦D≦10 μm,
−0.01D+0.57≦b/a≦−0.01D+0.97 hold, and
−0.7D+13≦c≦13,
where D denotes a value of an average particle diameter D50 of the active material particles,
a denotes a volume % of a volume fraction of the active material particles in the positive active material mixture layer,
b denotes a volume % of a volume fraction of a vacancy volume in the positive active material mixture layer and
c denotes a volume % of a volume fraction of the conductive additive particles in the positive active material mixture layer.
2. The lithium ion secondary battery according to claim 1 , wherein the active material particles comprise a lithium transition metal composite oxide.
3. The lithium ion secondary battery according to claim 2 , wherein the lithium transition metal composite oxide is represented by a chemical formula of Li a Ni x Mn y Co 1-x-y O 2 (0<a<1.3, 0<x≦0.6, 0<y<0.5).