Polylactic acid composition, foam molded article thereof and method of producing the same
A polylactic acid composition is produced with an MI value of 0.05 or more and 5 or less, the MI value being measured at 190° C. under a load of 21.6 kg in accordance with JIS K7210 (ISO 1133). A polylactic acid is crosslinked with a polyisocyanate to generate a cross-linked polylactic acid, including a large cross-linked polylactic acid molecule which inhibits foaming. The cross-linked polylactic acid is mechanically grinded-by applying a shear force to decrease a molecular weight of the large cross-linked polylactic acid molecule. The amount of the polyisocyanate combined is 0.4 to 5% by weight based on the polylactic acid. The grinding is conducted in supercritical condition of an inert gas. A foam molded article is made from the polylactic acid composition.
1. A method of producing a polylactic acid composition with an MI value of 0.05 or more and 5 or less, the MI value being measured at 190° C. under a load of 21.6 kg in accordance with JIS K7210 (ISO 1133), comprising:
crosslinking a polylactic acid with a polyisocyanate to generate a cross-linked polylactic acid, including a large cross-linked polylactic acid molecule which inhibits foaming, and
mechanically grinding the cross-linked polylactic acid, by applying a shear force to decrease a molecular weight of the large cross-linked polylactic acid molecule, the amount of the polyisocyanate combined being 0.4 to 5% by weight based on the polylactic acid, the grinding being conducted in supercritical condition of an inert gas, the shear force being applied in an orifice portion having a slit or a sleeve from which the polylactic acid composition is extruded, by allowing the cross-linked polylactic acid to pass through the orifice portion, the temperature in the orifice portion being from 160 to 180° C., and the pressure in the orifice portion being from 6 to 12 MPa.
2. The method according to claim 1 , wherein a number average molecular weight in a polystyrene equivalent of the polylactic acid composition obtained by the grinding measured by GPC is less than 1.5 million.
3. The method according to claim 1 , and selecting the polyisocyanate as one of triisocyanate, tetraisocyanate, diisocyanate, and any of the adduct forms of said polyisocyanates.
4. The method according to claim 1 , and adding 0.5 to 5% by weight of calcium carbonate or talc particle.
5. The method according to claim 1 , wherein the polylactic acid composition has a composition which does not contain high molecules having a molecular weight of 1.5 million or more in polystyrene equivalent.
6. The method according to claim 1 , wherein the grinding is conducted in supercritical condition of nitrogen gas, or the mixed gas of nitrogen gas and methanol.
7. A method of producing a foam molded article of a polylactic acid composition with an MI value of 0.05 or more and 5 or less, the MI value being measured at 190° C. under a load of 21.6 kg in accordance with JIS K7210 (ISO 1133), comprising:
crosslinking a polylactic acid with a polyisocyanate to generate a cross-linked polylactic acid, including a large cross-linked polylactic acid molecule which inhibits foaming,
mechanically grinding the cross-linked polylactic acid, by applying a shear force to decrease a molecular weight of the large cross-linked polylactic acid molecule, the amount of the polyisocyanate combined being 0.4 to 5% by weight based on polylactic acid, the grinding being conducted in supercritical condition of an inert gas, the grinding being conducted by the use of a device equipped with an injection molding machine (B) or an extrusion molding machine (G), an orifice portion (S) having a slit or a sleeve in which the shear force is applied and from which the polylactic acid composition is extruded, and a foaming mold (P), in supercritical condition of a foaming gas in the orifice portion (S), the shear force being applied by allowing the cross-linked polylactic acid to pass through the orifice portion, the temperature in the orifice portion being from 160 to 180° C., and the pressure in the orifice portion being from 6 to 12 Mpa, and
forming the foam molded article of the polylactic acid composition.
8. The method according to claim 7 , wherein a number average molecular weight in a polystyrene equivalent of the polylactic acid composition obtained by the grinding measured by GPC is less than 1.5 million.
9. The method according to claim 7 , and selecting the polyisocyanate as one of triisocyanate, tetraisocyanate, diisocyanate, and any of the adduct forms of said polyisocyanates.
10. The method according to claim 7 , and adding 0.5 to 5% by weight of calcium carbonate or talc particle.
11. The method according to claim 7 , wherein the polylactic acid composition has a composition which does not contain high molecules having a molecular weight of 1.5 million or more in polystyrene equivalent.
12. The method according to claim 7 , wherein the grinding is conducted in supercritical condition of nitrogen gas, or the mixed gas of nitrogen gas and methanol.