Process for producing phenol and method for regenerating catalyst deactivated in the process
A process for producing phenol is described in which a feed comprising alkylbenzene hydroperoxide is contacted with a cleavage catalyst under cleavage conditions effective to convert at least part of the hydroperoxide into phenol, the process is characterized in that at least a part of the deactivated catalyst is regenerated using a oxidizing material comprising hydrogen peroxide and then return to the process. A method of regenerating the cleavage catalyst is also described.
1. A process for producing phenol comprising:
(a) contacting a feed comprising alkylbenzene hydroperoxide with a cleavage catalyst comprising of a zeolite having a FAU, *BEA, MTW, or MOR framework type, and/or a solid-acid comprising a sulfated transition metal oxide under non-aqueous cleavage conditions effective to convert at least part of the alkylbenzene hydroperoxide to phenol;
(b) regenerating at least part of the cleavage catalyst by contacting the catalyst with an aqueous hydrogen peroxide solution; and
(c) returning at least part of the regenerated catalyst to step (a) after step (b), the regenerated catalyst comprising water on the catalyst.
2. The process of claim 1 , wherein the aqueous hydrogen peroxide solution has a concentration of hydrogen peroxide of from 3 wt % to 50 wt % based on the total weight of the aqueous solution.
3. The process of claim 1 , wherein the cleavage catalyst comprises a zeolite having a FAU framework type.
4. The process of claim 1 , wherein step (b) is conducted at a temperature of from 50° C. to 250° C.
5. The process of claim 1 , wherein step (b) is conducted at a pressure of from 200 kPa to 3000 kPa.
6. The process of claim 1 , wherein the weight ratio of hydrogen peroxide to the catalyst in step (b) is from 0.01 to 10.
7. The process of claim 1 , wherein the catalyst in step (b) is washed with a polar solvent prior to contacting with the oxidizing material.
8. The process of claim 7 , wherein the polar solvent comprises at least one of acetone, methanol, ethanol, and cyclohexanone.
9. The process of claim 1 , further comprising, prior to step (a):
(i) contacting an alkylbenzene with an oxygen-containing compound in the presence of an oxidation catalyst comprising a cyclic imide under oxidation conditions effective to produce an oxidation product comprising alkylbenzene hydroperoxide; and
(ii) supplying at least a portion of the oxidation product to the feed of step (a).
10. The process of claim 1 , wherein the alkylbenzene comprises cyclohexylbenzene, cumene, and/or sec-butylbenzene.
11. A method for regenerating a catalyst comprising contacting the catalyst with an oxidizing material comprising hydrogen peroxide, wherein the catalyst comprises a solid acid comprising a sulfated transition metal oxide deactivated in a cleavage process of alkylbenzene hydroperoxide to phenol.
12. The method of claim 11 , wherein the catalyst comprises sulfated zirconia.
13. The method of claim 11 , wherein the oxidizing material comprises an aqueous hydrogen peroxide solution.
14. The method of claim 13 , wherein the aqueous hydrogen peroxide solution has a concentration of hydrogen peroxide of from 3 wt % to 50 wt % based on the weight of the aqueous solution.
15. The method of claim 11 , wherein the catalyst is regenerated at a temperature of from 50° C. to 250° C.
16. The method of claim 11 , wherein the catalyst is regenerated at a pressure of from 200 kPa to 3000 kPa.
17. The method of claim 11 , wherein the weight ratio of hydrogen peroxide to the catalyst is from 0.01 to 10.
18. The method of claim 11 , wherein the catalyst is regenerated for a time period of from 0.5 hour to 5 days.
19. The method of claim 11 , wherein the catalyst comprises coke deposited on the catalyst before regeneration and at least 30 wt % of coke based on the weight of the coke deposited on the catalyst before regeneration is removed after regeneration.
20. The method of claim 11 , wherein the regenerated catalyst has a catalyst activity of from 50% to 120% of a fresh catalyst, the catalyst activity is measured by determining the conversion of alkylbenzene hydroperoxide to phenol under cleavage conditions including a temperature of about 20° C. to 200° C. and a pressure of 200 kPa to 2000 kPa.
21. The method of claim 11 , wherein the regenerated catalyst has a selectivity to phenol of from 70%-110% of a fresh catalyst, the catalyst selectivity is measured by determining the selectivity of phenol under cleavage conditions including a temperature of about 20° C. to 200° C. and a pressure of 200 kPa to 2000 kPa.
22. The method of claim 11 , wherein the alkylbenzene comprises cyclohexylbenzene, cumene, or sec-butylbenzene.
23. A method for regenerating a catalyst comprising a solid acid comprising a sulfated transition metal oxide deactivated in a cleavage process of cyclohexylbenzene hydroperoxide to phenol and cyclohexanone, the method comprising contacting the deactivated catalyst with an aqueous hydrogen peroxide solution under regeneration conditions including a temperature of from 50° C. to 250° C. and a pressure of from 200 kPa to 3000 kPa.
24. A method for producing phenol and/or cyclohexanone, the process comprising:
(a) hydroalkylating benzene with hydrogen in the presence of a hydroalkylation catalyst under conditions effective to produce a hydroalkylation reaction product comprising cyclohexylbenzene;
(b) separating at least a portion of the cyclohexylbenzene from the hydroalkylation reaction product;
(c) contacting at least a portion of the cyclohexylbenzene from the separating step (b) with an oxygen-containing compound in the presence of an oxidation catalyst comprising a cyclic imide under oxidation conditions effective to produce an oxidation product comprising cyclohexylbenzene hydroperoxide and cyclic imide catalyst;
(d) contacting at least a portion of the oxidation product comprising cyclohexylbenzene hydroperoxide with a cleavage catalyst comprising a zeolite having FAU, *BEA, MTW, or MOR framework type and/or a solid acid comprising a sulfated transition metal oxide under non-aqueous cleavage conditions effective to convert at least part of the cyclohexylbenzene hydroperoxide into phenol and/or cyclohexanone;
(e) regenerating at least part of the cleavage catalyst deactivated in step (d) by contacting the catalyst with an aqueous hydrogen peroxide solution; and
(f) returning at least part of the regenerated catalyst to step (d) after step (e), the regenerated catalyst comprising water on the catalyst.