Redox polymers for improved dirt and water resistance for elastomeric wall and roof coatings
The present invention provides elastomeric roof coatings and aqueous coating compositions of (i) an acrylic emulsion copolymer that comprises (ii) a reductant and has a high molecular weight, (iii) a combination of a hydrophilic polymeric dispersant and a pigment, extender or filler, and (iv) a multivalent transition metal ion or multivalent transition metal ion compound or salt. The composition and coating provide excellent swelling resistance and a balance of tensile and elongation in an acrylic roof coating composition.
1. An aqueous composition for coating roofing substrates comprise (i) one or more emulsion copolymer having a glass transition temperature (Tg) of from −45° C. to −10° C. having a weight average molecular weight of from 100,000 to 2,000,000, the emulsion copolymer being the copolymerization product of a monomer mixture of (a) from 74 wt. % to 97.75 wt. % of one or more C 4 to C 6 alkyl(meth)acrylates or a mixture thereof with up to 20 wt. % of a C 7 to C 24 alkyl(meth)acrylate to make a total of 80 to 94 wt. %, (b) from 2 to 20 wt. % of a hard vinyl monomer, and (c) from 0.25 wt. % to 3.0 wt. % of one or more ethylenically unsaturated monofunctional carboxylic acid group containing monomer, (ii) a reductant, (iii) a combination of one or more of a pigment, extender, filler and mixtures thereof with one or more hydrophilic polymeric dispersant in a total amount so that the composition has a pigment volume concentration (% PVC) of from 20 to 55, and (iv) one or more multivalent transition metal ion or multivalent transition metal ion compound or salt, wherein the monomer mixture comprises 10 wt. % or less of any vinyl aromatic monomer; and, further wherein, the monomer mixture comprises 11 wt. % or less of (meth)acrylonitrile, all monomer weight percents are based on the total solids in the monomer mixture.
2. The aqueous composition as claimed in claim 1 , wherein the emulsion copolymer is a single stage polymer.
3. The aqueous composition as claimed in claim 1 , wherein the (i) one or more emulsion copolymer further comprises the copolymerization product of (c) methacrylic acid or a mixture thereof with acrylic acid.
4. The aqueous composition as claimed in claim 1 , wherein the aqueous emulsion copolymer composition, further comprises the copolymerization product of a monomer mixture having monomer d) from 0.1 to 2 wt. %, based on the total solids in the monomer mixture, of an adhesion promoting ethylenically unsaturated monomer.
5. The aqueous composition as claimed in claim 1 , wherein the (iv) one or more multivalent transition metal ion or multivalent transition metal ion compound or salt is zinc oxide or zinc hydroxide.
6. An elastomeric pigmented roof coating comprising (i) one or more emulsion copolymer having a glass transition temperature (Tg) of from −45° C. to −10° C., having a weight average molecular weight of from 100,000 to 2,000,000, and being the copolymerization product of a monomer mixture of (a) from 74 wt. % to 97.75 wt. %, of one or more C 4 to C 6 alkyl(meth)acrylates, or a mixture thereof with up to 20 wt. % of a C 7 to C 24 alkyl(meth)acrylate to make a total of 80 to 94 wt. % (b) from 2 to 20 wt. % of a hard vinyl monomer, and (c) from 0.25 wt. % to 3.0 wt. % of one or more ethylenically unsaturated carboxylic acid group containing monomer, wherein the monomer mixture comprises 10 wt. % or less of any vinyl aromatic monomer, such as styrene; further wherein, the monomer mixture comprises 11 wt. % or less of (meth)acrylonitrile, all monomer weight percents are based on the total solids in the monomer mixture, (ii) a reductant, (iii) a combination of one or more of a pigment, extender, filler and mixtures thereof with one or more hydrophilic polymeric dispersant in a total amount so that the composition has a pigment volume concentration (% PVC) of from 20 to 55, and (iv) one or more multivalent transition metal ion or multivalent transition metal ion compound or salt.
7. The coating as claimed in claim 6 , wherein the (i) one or more emulsion copolymer further comprises the copolymerization product of (c) methacrylic acid or a mixture thereof with acrylic acid.
8. The coating as claimed in claim 6 , wherein the (i) one or more emulsion copolymer further comprises the copolymerization product of a monomer mixture having monomer d) from 0.1 to 2 wt. %, based on the total solids in the monomer mixture, of an adhesion promoting ethylenically unsaturated monomer.
9. The coating as claimed in claim 6 which comprises an elastomeric white roof coating.
10. A method of making an aqueous coating compositions as claimed in claim 1 , comprising redox initiation emulsion polymerizing in an aqueous medium the monomer mixture of monomers (a), (b), (c), and, if included, the vinyl aromatic monomer and/or the (meth)acrylonitrile in the presence of an excess of (ii) reductant to form (i) a copolymer; and,
combining the copolymer (i) and excess (ii) reductant with (iii) a combination of one or more of a pigment, extender, filler and mixtures thereof with one or more hydrophilic polymeric dispersant in a total amount so that the composition has a pigment volume concentration (% PVC) of from 20 to 55, and (iv) one or more multivalent transition metal ion or multivalent transition metal ion compound or salt.