Friction stir method and a pair of workpieces joined by such method
A friction stir method comprises causing a rotating probe ( 1 ) of a friction stir tool to enter a workpiece or a joint between a pair of workpieces ( 89 ), the or each workpiece being a low conductivity, high melting point metal or metal alloy. The probe ( 1 ) extends from a shoulder ( 4 ), or between shoulders, in contact with the workpiece(s) and rotates relative to the or each shoulder.
1. A method for joining a pair of workpieces, the steps of the method comprising:
causing a rotating probe of a friction stir welding tool to enter a workpiece or a joint region between a pair of workpieces, each workpiece being a low conductivity, high melting point metal or metal alloy, with a melting temperature above that of aluminum and a thermal conductivity less than that of aluminum, the probe extending from a shoulder and rotating relative to the shoulder, the shoulder constructed of more than one piece, the piece nearer the probe having a high melting point and being an insert defined around an aperture through which the probe extends, the working surface of all the pieces of the shoulder being in contact with the workpieces during joining and not rotating relative to the workpieces, the heat required for joining the workpieces being generated only by the rotating probe.
2. A method according to claim 1 , further comprising moving the tool along a joint line between the workpieces.
3. A method according to claim 1 , further comprising moving the tool along a line extending along the workpiece.
4. A method according to claim 1 , wherein the shoulder defines a slide member.
5. A method according to claim 1 , wherein the shoulder is shaped to conform with the surface or surfaces of the workpieces against which it abuts.
6. A method according to claim 1 , wherein one or both of the probe and the shoulder is provided with a surface coating or surface treatment affecting one or more of the characteristics, of friction, wear resistance, temperature resistance, diffusion resistance, reactivity, and solid state lubrication.
7. A method according to claim 1 , further comprising supplying a shielding gas to the region between the shoulder and the workpieces.
8. A method according to claim 1 , further comprising supplying coolant and/or lubricant to the region between the shoulder and the workpieces.
9. A method according to claim 1 , wherein each workpiece is selected from the group comprising:
Ti and all alloys
Fe, steels and other alloys
Ni and alloys
V and alloys
Cr and alloys
Mn and alloys
Co and alloys
Zr and alloys
Pd and alloys
Hf and alloys
Pt and alloys.
10. A method according to claim 2 or claim 3 , wherein the probe is retracted, while rotating, as the tool approaches the end of the line, while the shoulder remains in contact with the workpieces.
11. A method according to claim 1 , wherein the melting point of the metal or metal alloy is greater than 700° C.
12. A method according to claim 1 , wherein the thermal conductivity of the metal or metal alloy is less than 250 W/mK.
13. A method according to claim 1 wherein the probe extends from a single shoulder in contact with the workpieces.