Polysulfide treatment of carbon black filler and elastomeric compositions with polysulfide treated carbon black
A chemically treated carbon black product is provided, which includes a pellet having an agglomerated mass of carbon black aggregates densified in a generally spheroidal form. The carbon black aggregates have polysulfide adsorbed on surfaces thereof. The polysulfide is thereby distributed throughout the pellet. Elastomeric compositions containing the chemically treated carbon black are also provided, and exhibit a reduction in hysteresis and equivalent or better abrasion resistance. A method for manufacturing the treated carbon black product is also disclosed.
1. A treated carbon black product, comprising:
carbon black aggregates having non-organic polysulfide salt adsorbed on surfaces thereof, wherein the non-organic polysulfide salt is adsorbed on a fraction of the surfaces of the carbon black aggregates, and the non-organic polysulfide salt exists at discrete, spaced apart regions at the surfaces of the aggregates.
2. The treated carbon black product of claim 1 , wherein the carbon black aggregates are in the form of a pellet including an agglomerated mass of the carbon black aggregates.
3. The treated carbon black product of claim 2 , wherein the non-organic polysulfide salt is evenly distributed throughout the pellet.
4. The treated carbon black product of claim 1 , wherein the non-organic polysulfide salt is present in an amount from about 0.1% to about 10% by weight of the aggregate.
5. The treated carbon black product of claim 1 , wherein the non-organic polysulfide salt includes S x , with x being from 2 to 100.
6. A treated carbon black product, comprising:
carbon black aggregates having non-organic polysulfide salt adsorbed on surfaces thereof, wherein the surfaces of the carbon black aggregates are also oxidized.
7. The treated carbon black product of claim 1 , wherein adsorption of the non-organic polysulfide salt on the surface of the carbon black aggregates results in a depression in ASTM D6556 nitrogen adsorption of between about 0.1 percent and about 10 percent.
8. An elastomeric composition, comprising:
an elastomer; and
carbon black aggregates having non-organic polysulfide salt adsorbed on surfaces thereof.
9. The elastomeric composition of claim 8 , wherein the elastomer is selected from a group consisting of natural rubber, emulsion SBR, solution SBR, functional solution SBR, polybutadiene, polyisoprene, EPDM, nitrile, butyl, halogenated butyl, silicone rubber and any combination thereof.
10. The elastomeric composition of claim 8 , further comprising a cure package including at least one of sulfur and an accelerator.
11. The elastomeric composition of claim 10 , wherein the accelerator is sulfur-containing and an amount of the accelerator is selected to account for the presence of the non-organic polysulfide salt adsorbed on the surfaces of the carbon black aggregates.