Inorganic-inorganic composite material and method for producing the same
Process for producing an inorganic-inorganic composite material, in which an open-pore, crystalline oxide ceramic shaped part is produced from an oxide ceramic powder or a powder of an oxide ceramic mixture after shape-imparting processing and presintering, an infiltration substance is applied to this shaped part in vacuo and at room temperature, and the oxide ceramic is sintered in a densifying manner under an air atmosphere and at ambient pressure to form an inorganic-inorganic composite material.
1. A sintered inorganic-inorganic composite material, comprising
(a) a translucent inner region made from a crystalline oxide ceramic resulting from an open-pore structure and consisting of zirconium oxide and one or more oxides selected from the group consisting of elements of groups IIIb and IVb, and
(b) a layer of an infiltration substance which at least partially surrounds or covers the inner region, the infiltration substance layer resulting from sintering a precursor that was infiltrated at room temperature, the precursor selected from a precursor of a nonmetallic-inorganic phase, a precursor of an amorphous glass phase, a precursor of a hydrolysable compound of a metal, or a precursor from an alkoxide of a metal selected from the group of elements consisting of Al, Ti, Zr or Si, and
(c) a theoretical density of >99.5%,a biaxial strength of not less than 800 MPa and a fracture toughness of more than 6.5 MPa m 1/2 .
2. The composite material as claimed in claim 1 , wherein the crystalline oxide ceramic consists of zirconium oxide and additions of yttrium oxide.
3. The composite material as claimed in claim 1 , wherein the zirconium oxide consists of additions of from 2 to 10 mol %, yttrium oxide, or of 2.5 to 15 mol % cerium oxide, or 2.5 to 5 mol % erbium oxide or 2.5 to 5 mol % scandium oxide, or 0.1 to 15 mol % titanium dioxide or mixtures of two or more of the abovementioned oxides in the quantities indicated.
4. The composite material as claimed in claim 1 , wherein the zirconium oxide consists of additions of from 2 to 4 mol % yttrium oxide.
5. The composite material as claimed in claim 1 , wherein the zirconium oxide is tetragonal zirconium oxide.
6. The composite material as claimed in claim 1 , wherein the precursor of the non-metallic-inorganic phase comprises ionogenic or covalent compounds of the elements of groups Ia, IIa, IIIa, IVa, IIIb, IVb, Vb, VIb, VIIb, VIIIb, where “a” denotes the main groups and “b” denotes the transition groups of the periodic system of the elements.
7. The composite material as claimed in claim 1 , wherein the infiltration substance comprises covalent bonds of Si and/or Zr.
8. The composite material as claimed in claim 1 , wherein the infiltration substance comprises ionogenic compounds.
9. The composite material as claimed in claim 8 , wherein the ionogenic compounds comprise Ce, Mn, V, Fe or mixtures of said elements.
10. The composite material as claimed in claim 1 , wherein the amorphous glass phase is silicate glass.
11. The composite material as claimed in claim 10 , wherein the silicate glass is an alkali-metal-free silicate glass.
12. The composite material as claimed in claim 1 , wherein the infiltration substance comprises tetraethyl orthosilicate as a hydrolysable compound.
13. The composite material as claimed in claim 1 , wherein the infiltration substance comprises alkoxides of silicon or aluminum.
14. The composite material as claimed in claim 1 , wherein the inner region is translucent and the layer of infiltration substance is cloudy-white.
15. The composite material as claimed in claim 1 , wherein the inner region has a translucency which corresponds to that of hot isostatically pressed sintered ceramics.
16. A method of using the inorganic-inorganic composite material as claimed in claim 1 , in the dental sector, as a dental restoration, implant, implant part or orthodontic product.
17. The method of claim 16 , wherein the dental restoration is a dental framework, a crown, a partial crown, a bridge, a cap, a shell, a veneer, an abutment or a post structure.