High-throughput solution processing of large scale graphene and device applications
A method of producing carbon macro-molecular structures includes dissolving a graphitic material in a solvent to provide a suspension of carbon-based macro-molecular structures in the solvent, and obtaining a plurality of the carbon macro-molecular structures from the suspension. The plurality of carbon macro-molecular structures obtained from the suspension each consists essentially of carbon. A material according to some embodiments of the current invention is produced according to the method of producing carbon macro-molecular structures. An electrical, electronic or electro-optic device includes material produced according to the methods of the current invention. A composite material according to some embodiments of the current invention has carbon macro-molecular structures produced according to methods of producing carbon macro-molecular structures according to some embodiments of the current invention. A hydrogen storage device according to some embodiments of the current invention has carbon macro-molecular structures produced according to methods of producing carbon macro-molecular structures according to some embodiments of the current invention. An electrode according to some embodiments of the current invention has carbon macro-molecular structures produced according to methods of producing carbon macro-molecular structures according to some embodiments of the current invention.
1. An electrode for an electrical, electronic or electro-optic device, comprising:
a plurality substantially planar graphene-based structures; and
a plurality of carbon nanotubes which are in electrical connection with at least two of said plurality of substantially planar graphene-based structures,
wherein said substantially planar graphene-based structures are each single-sheet graphene-based structures having an area of at least 1 μm 2 ,
wherein said plurality of carbon nanotubes provide electrical connection between otherwise electrically isolated substantially planar graphene-based structures, and
wherein said graphene-based structures have a carbon to oxygen atomic ratio of at least 12:1.
2. An electrode according to claim 1 , wherein said electrode has a thickness selected in accordance with a preselected electrical conductivity for said electrode.
3. An electrode according to claim 1 , further comprising at least one of semiconducting nanorods or conducting nanorods.
4. An electrode according to claim 1 , further comprising a layer of an electrically conducting material in addition to a layer formed by said substantially planar graphene-based structures and said carbon nanotubes to provide at least a two layer electrode.
5. An electrode according to claim 1 , wherein said electrode is sufficiently transparent to electromagnetic radiation in an operating range of wavelengths of an electro-optic device to be used as a transparent electrode.
6. An electrical, electronic or electro-optic device comprising an electrode, said electrode comprising:
a plurality substantially planar graphene-based structures; and
a plurality of carbon nanotubes which are in electrical connection with at least two of said plurality of substantially planar graphene-based structures,
wherein said substantially planar graphene-based structures are each single-sheet graphene-based structures having an area of at least 1 μm 2 ,
wherein said plurality of carbon nanotubes provide electrical connection between otherwise electrically isolated substantially planar graphene-based structures, and
wherein said graphene-based structures have a carbon to oxygen atomic ratio of at least 12:1.
7. An electrode according to claim 6 , further comprising at least one of semiconducting nanorods or conducting nanorods.
8. An electrical, electronic or electro-optic device according to claim 6 , said electrode further comprising a layer of an electrically conducting material in addition to a layer formed by said substantially planar graphene-based structures and said carbon nanotubes to provide at least a two layer electrode.
9. An electrical, electronic or electro-optic device according to claim 6 , wherein said electrode is sufficiently transparent to electromagnetic radiation in an operating range of wavelengths of an electro-optic device to be used as a transparent electrode.
10. An electrical, electronic or electro-optic device according to claim 6 , wherein said electrical, electronic or electro-optic device is at least one of a capacitor, a supercapacitor, a diode, a light emitting diode, a photodiode, a transistor, a photovoltaic cell, a battery, a display device, a field emission display, or an assembly incorporating any combination thereof.
11. A composition comprising a matrix material and graphene-based structures,
wherein the graphene-based structures are produced according to a method comprising:
dissolving a graphitic material in an anhydrous solvent to provide a suspension of carbon-based macro-molecular structures in said solvent; and
obtaining a plurality of said graphene-based structures from said suspension,
wherein said plurality of graphene-based structures obtained from said suspension each consists essentially of carbon,
wherein the graphene-based structures are blended with said matrix material,
wherein said graphene-based structures act to alter at least one of an electrical, structural or mechanical property of said matrix material,
wherein said graphene-based structures are each single-sheet graphene-based structures having an area of at least 1 μm 2 , and
wherein said graphene-based structures have a carbon to oxygen atomic ratio of at least 12:1.
12. A composition according to claim 11 , wherein said matrix material is a polymer.
13. A composition according to claim 11 , wherein said matrix material is a polymer composite.
14. A composition according to claim 11 , wherein said matrix material is a conducting polymer.
15. A composition according to claim 11 , wherein said composition is for use in electronic devices.
16. A composition according to claim 11 , wherein said composition is for use in mechanical devices.
17. A composition according to claim 11 , wherein said graphene-based structures are each single-sheet graphene-based structures having an area of at least 20 μm 2 .
18. A composition according to claim 11 , wherein said composition further comprises a plurality of carbon nanotubes, and
wherein said plurality of carbon nanotubes provide electrical connection between at least some of said single-sheet graphene-based structures.
19. A composition according to claim 18 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 55% at an operating wavelength and a sheet resistance less than 700Ω/□.
20. A composition according to claim 18 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 55% at an operating wavelength and a sheet resistance less than 44Ω/□.
21. A composition according to claim 18 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 87% at an operating wavelength and a sheet resistance less than 600Ω/□.
22. A composition, comprising:
a matrix material; and
graphene-based structures blended with said matrix material,
wherein said graphene-based structures act to alter at least one of an electrical, structural or mechanical property of said matrix material,
wherein said graphene-based structures are each single-sheet graphene-based structures having an area of at least 1 μm 2 , and
wherein said graphene-based structures have a carbon to oxygen atomic ratio of at least 12:1.
23. A composition according to claim 22 , wherein said graphene-based structures are each single-sheet graphene-based structures having an area of at least 20 μm 2 .
24. A composition according to claim 22 , further comprising:
a plurality of carbon nanotubes blended with said matrix material,
wherein said plurality of carbon nanotubes provide electrical connection between at least some of said single-sheet graphene-based structures.
25. A composition according to claim 24 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 55% at an operating wavelength and a sheet resistance less than 700Ω/□.
26. A composition according to claim 24 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 55% at an operating wavelength and a sheet resistance less than 44Ω/□.
27. A composition according to claim 24 , wherein said composition is suitable to be formed into a transparent electrode having a transparency of at least 87% at an operating wavelength and a sheet resistance less than 600Ω/□.
28. A composition according to claim 11 , wherein said graphene-based structures further comprise nitrogen such that a carbon to nitrogen atomic ratio is within the range of 8:1.5 to 12:0.7.
29. A composition according to claim 22 , wherein said graphene-based structures further comprise nitrogen such that a carbon to nitrogen atomic ratio is within the range of 8:1.5 to 12:0.7.